Anistropy pinning of domain walls in soft magnetic material

W. K. Ho,R. Schafer,J. Yamasaki,A. Hubert,F. Humphrey

DOI: https://doi.org/10.1109/INTMAG.1989.690205

1989-03-28

Abstract:Annealing an unsaturated sample of soft amorphous magnetic ribbon or thin film displays a characteristically pinned hysteresis loop. 1,2. In this paper narrow ribbons of a cobalt-rich nonmagnetostrictive metallic glass (dimensiobs 75mmxlrnmx35um) are studied in more detail in order to understand the characteristics of this phenomenon. Figure 1 shows a characteristic hysteresis curve obtained after annealing when the sample is exposed to a moderate magnetic field of a few Oersteds maximum. This loop can be unstable at high maximum fields where it can change to that of a normal sample with high demagnetization field. The model that was used assumed that the anisotropy induced by the anneal followed the direction of the magnetization at the time of the anneal even when the magnetization made a domain wall. This induced helical anisotropy could then trap the wall as it passed the site creating a loop as seen in Fig. 1. The model has now been confirmed by direct observation of the pinning site. Figure 2 shows an example of a direct observation of the domain wall and the pinning site, obtained with the digitally enhanced magnetooptic Kerr microscope adjusted to observe the 1ongitudina.l Kerr effect along the axis prependicular to the ribbon axis 3. A finger shaped domain can be seen on the left with a single domain on the right. Even without a domain wall on the right, a contrast appears at the pinning site indicating a "quasi wall"-a magnetization excursion with a zero angle of total rotation, induced by the local anisotropy.