Abstract:Cellulose is a strong contender for the development of sustainably resourced biodegradable material composites supporting circular economy. Nanofibrillar cellulose-comprising materials are among the most promising lignocellulose derivatives. Currently, their production capacity and economy are hindered by high chemical and energy consumption, the latter primarily during mechanical fibrillation of native fiber in aqueous suspension and the negative limitation of very low solid content associated with the gel-like properties of the resulting final product. The application of oxygen gas barrier discharge (DBD) plasma on dry cellulose fiber, as reported here, is considered novel in achieving onward nanofibrillation. At this early stage, though, simple laboratory DBD equipment precludes the study of overall efficiency. Example fiber was taken from paper pulp manufacture but may not be limited to wood source. The oxygen plasma was seen to etch the microcellulose fiber structure, simultaneously oxidizing the glue-functioning hemicellulose, rendering it soluble, so that nanopolymer crystalline-based cellulose fibrils can be readily released at the surface of the host refined microfiber at the point of application, forming micro nanofibrillated cellulose structure (MNFC) at previously uneconomic higher solid content. Eliminating the need for liquid water during precursor process treatment is considered potentially transformative with respect to production feasibility, end-product transportation and application. 纤维素是开发支持循环经济的可持续资源可生物降解材料复合材料的有力竞争者. 含纳米纤维纤维素的材料是最有前景的木质纤维素衍生物之一. 目前,它们的生产能力和经济性受到高化学和能源消耗的阻碍,后者主要是在水悬浮液中天然纤维的机械原纤化过程中,以及与最终产品的凝胶状特性相关的极低固体含量的负面限制. 如本文所述,氧气阻挡放电(DBD)等离子体在干纤维素纤维上的应用被认为是实现向前纳米纤维化的新方法. 然而,在这个早期阶段,简单的实验室DBD设备阻碍了对整体效率的研究. 示例纤维取自纸浆制造,但可能不限于木材来源. 观察到氧等离子体蚀刻微孔纤维素纤维结构,同时氧化起胶作用的半纤维素,使其可溶,从而在应用点,纳米聚合物结晶基纤维素原纤维可以很容易地在宿主精制微纤维的表面释放,在以前不经济的较高固体含量下形成微纳米纤维化纤维素结构(MNFC). 在前体工艺处理过程中消除对液态水的需求被认为在生产可行性、最终产品运输和应用方面具有潜在的变革性.

Fabrication of microfibrillated cellulose from biomass by use of carbon nitride with high nitrogen/carbon ratio

A COMPARATIVE STUDY OF CELLULOSE NANOWHISKERS (cnws) AND CELLULOSE NANOFIBERS (Cnfs)

Preparation and Characterization of Nanofibrillated Cellulose from Bamboo Fiber Via Ultrasonication Assisted by Repulsive Effect

One-pot Preparation of Micro-Fibrillated Cellulose Fiber (MCF) Through the Synergistic Action of G-C3n4 and a Diluted Acid

Surface-modified and Oven-Dried Microfibrillated Cellulose Reinforced Biocomposites: Cellulose Network Enabled High Performance.

Production of Micro Nanofibrillated Cellulose from Prerefined Fiber via a Dry Dielectric Barrier Discharge (DBD) Oxygen Plasma-Treated Powder Precursor

Isolation of Cellulose Nanofibers (CNFs) based on Ball-milling Technique Combined with Supercritical Carbon dioxide/ethanol Pretreatment

High-yield and scalable cellulose nanomesh preparation via dilute acid vapor and enzymatic hydrolysis-mediated nanofabrication

Preparation of microfibrillated cellulose by in situ and one step method using calcium hydroxide as swelling and grinding agent

Isolation and characterization of microfibrillated cellulose and nanofibrillated cellulose with "biomechanical hotspots"

Highly efficient and green micro/nano cellulose preparation with micro-nano bubbles from mild alkali pretreated bagasse

From unavoidable food waste to advanced biomaterials: microfibrilated lignocellulose production by microwave-assisted hydrothermal treatment of cassava peel and almond hull

Micro- and nano-hybrid cellulose fibers prepared by straightforward and high-efficiency hot water soaking-assisted colloid grinding for high-performance cellulose paper

Extraction and characterization of microfibrillated cellulose (MFC) from Rhododendron ponticum isolated using cryocrush pre-treatment and its potential for mycelium cultivation

One-pot green extraction of high charge density cellulose nanocrystals with high yield for bionanocomposites

Fabrication and Characterization of Microfibrillated Cellulose and Collagen Composite Films

Preparation of Microfibrillated Cellulose from Wood Pulp Through Carbamate Modification and Colloid Milling

High-Consistency Mechano-Enzymatic Fibrillation of Bamboo Pulp Fibers to Produce Precursors for Highly Fibrillated Cellulose and Dense Films with Multifunctionalities

A facile approach for preparing nanofibrillated cellulose from bleached corn stalk with tailored surface functions

Producing Cellulose Microfibrils at a High Solid Content with and without Mechanical or Enzymatic Pretreatment

Direct Carboxymethylation of Cellulose Fibers by Ternary Reactive Deep Eutectic Solvents for the Preparation of High-Yield Cellulose Nanofibrils