Deep insight of unique phase transition behaviors and mechanism in Zr2Co-H isotope system with ultra-low equilibrium pressure

Yang Liu,Pan-Pan Zhou,Xue-Zhang Xiao,Jia-Cheng Qi,Jia-Peng Bi,Tiao Ying,Xing-Wen Feng,Yan Shi,Wen-Hua Luo,Li-Xin Chen

DOI: https://doi.org/10.1007/s12598-023-02350-9

IF: 6.318

2023-11-09

Rare Metals

Abstract:Efficient capture, safe storage and release of tritium from the international thermonuclear experimental reactor (ITER) reaction exhaust gas is a perplexing problem, and the development of an efficient tritium-getter material with ultra-low hydrogenation equilibrium pressure is considered as a reliable way. In this work, Zr 2 Co alloy was selected as a tritium-getter material and prepared through induction levitation melting. Fundamental performance test results show that Zr 2 Co exhibits an ultra-low hydrogenation equilibrium pressure of 3.22 × 10 –6 Pa at 25 °C and excellent hydriding kinetics under a low hydrogen pressure of 0.005 MPa. Interestingly, unique phase transition behaviors were presented in Zr 2 Co-H system. Specifically, Zr 2 CoH 5 formed by Zr 2 Co hydrogenated at room temperature is initially decomposed into ZrH 2 and ZrCoH 3 at 200 °C. With the temperature increasing to 350 °C, ZrCoH 3 is dehydrogenated to ZrCo, and then ZrCo further reacts with ZrH 2 at 650 °C to reform Zr 2 Co and hydrogen. Among the staged phase transition pathways during dehydrogenation, the decomposition of Zr 2 CoH 5 occurs preferentially, which is well accordance with both the smallest reaction energy barrier and the maximum reaction spontaneity that are determined respectively from kinetics activation energy and thermodynamics Gibbs free energy. Furthermore, first principles calculation results indicate that the stronger binding of hydrogen in interstitial environments of ZrCoH 3 and ZrH 2 triggers the hydrogen-stabilized phase transformation of Zr 2 CoH 5 . The unique phase transition mechanisms in Zr 2 Co-H system can shed light on the further exploration and regulation of analogous staged phase transition of hydrogen storage materials.

materials science, multidisciplinary,metallurgy & metallurgical engineering