Enhancing disproportionation resistance of Zr 2 Co-based alloys by regulating the binding energy of H atom

Yang Liu,Zhiyi Yang,Xuezhang Xiao,Panpan Zhou,Yuxiao Jia,Xingwen Feng,Jiangfeng Song,Yan Shi,Changan Chen,Wenhua Luo,Lixin Chen

DOI: https://doi.org/10.1016/j.renene.2024.121153

IF: 8.7

2024-08-22

Renewable Energy

Abstract:Considering the scarcity and radioactivity of tritium, developing efficient tritium recovery and storage technology is essential for the safety and stability of nuclear fusion reactions. Zr 2 Co alloy is a prospective tritium-getter material, while its poor disproportionation resistance limits the practical application. To address this issue, Zr 2 Co alloy was modified by alloying and Zr 2 Co 0.9 M 0.1 (M = Cr, Mn, Fe, Ni, Cu) alloys were prepared. Performance test results indicate that all Zr 2 Co 0.9 M 0.1 alloys exhibit the main phase corresponding to Zr 2 Co phase and their hydrogenation phases belong to Zr 2 CoH 5 phase. Alloying improves the hydrogen storage capacity and reduces the hydrogenation equilibrium pressure of Zr 2 Co alloy. Zr 2 Co 0.9 Cr 0.1 , Zr 2 Co 0.9 Mn 0.1 , and Zr 2 Co 0.9 Fe 0.1 alloys have hydrogen storage capacities above 2 wt% and hydrogenation equilibrium pressures approximately 10 −7 Pa at room temperature. Furthermore, Zr 2 Co 0.9 M 0.1 alloys have better disproportionation resistance compared to Zr 2 Co alloy. Notably, Zr 2 Co 0.9 Fe 0.1 and Zr 2 Co 0.9 Ni 0.1 alloys possess interstitial sites with moderate hydrogen binding energies, resulting in stronger disproportionation resistance than that of other alloys. Therefore, Zr 2 Co 0.9 Fe 0.1 alloy is the most promising tritium-getter material among the studied materials. The cycling performance of Zr 2 Co 0.9 Fe0.1 alloy is investigated and a superior capacity retention of 94 % is found out. This work shed light on the further exploration of tritium-getter materials.

energy & fuels,green & sustainable science & technology