A highly efficient and suitable spectral profile Cr3+-doped garnet near-infrared emitting phosphor for regulating photomorphogenesis of plants

Xikun Zou,Xiaojun Wang,Haoran Zhang,Yunyan Kang,Xian Yang,Xuejie Zhang,Maxim S. Molokeev,Bingfu Lei

DOI: https://doi.org/10.1016/j.cej.2021.132003

IF: 15.1

2022-01-01

Chemical Engineering Journal

Abstract:Far-red/phytochrome (PFR) plays a key role in photomorphogenesis of plants. However, how to obtain a near-infrared (NIR) emitting phosphor with high external quantum efficiency (EQE), suitable spectral profile, and low thermal quenching remains a huge challenge. Herein, a NIR phosphor, Gd2.4Lu0.6Ga4AlO12:Cr3+,H3BO3 (GLGA:Cr3+) was developed via regulating the crystal field environment and adding fluxes, which exhibits a peak maximum at 728 nm with a relatively narrow full-width at half maximum (FWHM) of 107 nm, matching well with the absorption band of PFR. Upon 450 nm excitation, the internal quantum efficiency (IQE) and EQE of the optimal phosphor are 90.3% and 32.0%, respectively. At 423 K, the integrated emission intensity of the investigated phosphor is about 75% of that at room temperature. Benefiting from the excellent optical performance, a NIR phosphor-converted light-emitting diode (pc-LED) was fabricated, which shows a NIR output power of 505.99 mW and photoelectric conversion efficiency of 11.24% at 300 mA. Moreover, plant growth experiments demonstrate that the biomass of pea seedlings is increased by 67.72% under supplementary NIR light irradiation. The findings of this research will motivate further research on new Cr3+-doped NIR phosphors for regulating photomorphogenesis of plants.

engineering, chemical, environmental

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop a near - infrared (NIR) - emitting phosphor that is efficient and has spectral characteristics suitable for the regulation of plant photomorphogenesis. Specifically, the researchers developed a Cr³⁺ - doped garnet - type NIR - emitting phosphor (Gd₂.₄Lu₀.₆Ga₄AlO₁₂:Cr³⁺, H₃BO₃). This phosphor has a peak emission at 728 nm and a full - width at half - maximum (FWHM) of 107 nm, which matches very well with the absorption band of plant far - red light/phytochrome (PFR). The paper also explores how to optimize the optical properties of the phosphor by adjusting the crystal - field environment and adding a flux, in order to achieve high external quantum efficiency (EQE), low thermal quenching, and ultimately be applied to the manufacture of NIR light - converting LEDs (pc - LEDs) for enhancing plant growth. The research results show that using this NIR pc - LED for supplementary lighting can significantly increase the biomass of pea seedlings by 67.72%. These findings provide an important reference for the future development of new Cr³⁺ - doped NIR phosphors for the regulation of plant photomorphogenesis.