Fabrication of oxygen-rich vacant 3D Zn–CuBi 2 O 4 /MMT photocatalysts and the enhancement of its photocatalytic performance

wenyuan Tan,Hongxia Sun,Wenfei Li,Yong Huang,Huan Zhang,Xiaofang Zhang,Wenyuan Tan

DOI: https://doi.org/10.1016/j.ceramint.2023.11.056

IF: 5.532

2023-12-07

Ceramics International

Abstract:Semiconductor catalytic materials have excellent photocatalytic degradation performance for organic pollutants, and photocatalytic degradation is considered to be the most promising technology for environmental pollution treatment. Bismuth-based bimetallic oxide CuBi 2 O 4 is widely recognized as one of the most valuable and promising semiconductor photocatalytic materials because of its narrow bandwidth, strong visible light absorption and excellent chemical stability. To further improve the photocatalytic activity of CuBi 2 O 4 , the Zn-doped CuBi 2 O 4 /montmorillonite composites were prepared by employing a synergistic control strategy of doping and oxygen vacancies (OVs), which efficiently regulated the electronic structure and the number of active sites to achieve a rapid separation of photogenerated charges. The doping of zn 2+ significantly increased the quantity of oxygen vacancies in the prepared materials. The BET revealed that the incorporation of montmorillonite (MMT) greatly increased the specific surface area of CuBi 2 O 4 . The experimental findings indicated that 5 % Zn–CuBi 2 O 4 /MMT0.6 possessed abundant oxygen vacancies and longer fluorescence lifetime, resulting in better photocatalytic performance. The removal rate of butyl xanthate was 99.31 % in 40 min, and the removal rate of tetracycline hydrochloride (TC) was 93.17 % in 180 min. The 5 % Zn–CuBi 2 O 4 /MMT0.6 could effectively inhibit e − /h + complexation and provide richer catalytic active sites by doping to construct a flower-like oxygen-rich vacancy defect structure, which significantly improves its catalytic performance. The results of the cycling experiments showed that the stability and reproducibility of the 5 % Zn–CuBi 2 O 4 /MMT0.6 composites were excellent, the present study provides an innovative idea for the development of efficient and stable visible light photocatalytic applications.

materials science, ceramics