Microstructure characteristics, degradation behaviors and film formation mechanism of Zn-1Mg-0.25Nd-xSn in the Kokubo's electrolyte
Yun Liu,Yuan Zhang,Rui-Ning Zheng,Ya-Qi Zheng,Lian-Sheng Chen
DOI: https://doi.org/10.1016/j.matchar.2021.111034
IF: 4.537
2021-04-01
Materials Characterization
Abstract:<p>Till now, the novel Zn-based alloys have attracted extensive attention, due to the excessive dissolution rate in the Mg-based alloys and the detrimental products in the Fe-based biomaterials. In this study, the novel degradable Zn-1 Mg-0.25Nd-<em>x</em>Sn alloys were fabricated, and the microstructure, degradation and film formation mechanism were investigated through scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron probe micro-analyzer (EPMA), atomic force microscopy (AFM), confocal laser scanning microscopy (3D/CLSM) and X-ray photoelectron spectroscopy (XPS). The results indicated that the morphology of interdendritic β-lamellar and primary η-Zn obviously changed as the Sn contents increased, whilst the corrosion initiates as a consequence of relative Volta potential differences between the Zn-rich and micro-eutectic phases. Therein, the optimalizing corrosion rate was obtained in the Zn-1 Mg-0.25Nd-0.3Sn, which was associated with the formation of insoluble Zn<sub>5</sub>(OH)<sub>8</sub>Cl<sub>2</sub>, Zn<sub>3</sub>(PO<sub>4</sub>)<sub>2</sub>, Sn(OH)<sub>2</sub>/Sn(OH)<sub>4</sub>, reducing the reaction activities of the Zn matrix. Besides, the REs-rich products incorporated into the passive layer and absorbed OH<sup>−</sup>, forming a uniform and dense degradation layer. However, as the Sn contents further increased, the formation of abundant micro-galvanic nucleation sites facilitates the metastable pits dissolution and the probability of transition from metastable to stable.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing