Optimization of areca leaf sheath nanolignin synthesis by a mechanical method for in situ modification of ultra-low molar ratio urea-formaldehyde adhesives

Muhammad Rasyidur Ridho,Muhammad Adly Rahandi Lubis,Deded Sarip Nawawi,Widya Fatriasari

DOI: https://doi.org/10.1016/j.ijbiomac.2024.132614

Abstract:This study addresses the optimization of the nanolignin preparation method from the areca leaf sheath (ALS) by a mechanical process using a high shear homogenizer at 13,000-16,000 rpm for 1-4 h and its application in enhancing the performance of ultralow molar ratio urea-formaldehyde (UF) adhesive. Response surface methodology (RSM) with a central composite design (CCD) model was used to determine the optimum nanolignin preparation method. The mathematical model obtained was quadratic for the particle size response and linear for the zeta potential response. Under the optimum conditions, a speed of 16,000 rpm for 4 h resulted in a particle size of 227.7 nm and a zeta potential of -18.57 mV with a high desirability value of 0.970. FE-SEM revealed that the characteristic changes of lignin to nanolignin occur from an irregular or nonuniform shape to an oval shape with uniform particles. Nanolignin was introduced during the addition reaction of UF resin synthesis. UF modified with nanolignin (UF-NL) was analyzed for its adhesive characteristics, functional groups, crystallinity, and thermomechanical properties. The UF-NL adhesive had a slightly greater solid content (73.23 %) than the UF adhesive, a gelation time of 4.10 min, and a viscosity of 1066 mPa.s. The UF-NL adhesive had similar functional groups as the UF adhesive, with a lower crystallinity of 59.73 %. Compared with the control plywood which has a tensile shear strength value of 0.79 MPa, the plywood bonded with UF-NL had a greater tensile shear strength of 1.07 MPa, with a lower formaldehyde emission of 0.065 mg/L.