Crystal structure, microwave dielectric properties, and dielectric resonant antenna studies of novel low-permittivity CoAl2O4 spinel ceramics

Yi Ding,Cheng Chao Hu,Wei Qin Sheng,Kai Xin Song,Bing Liu

DOI: https://doi.org/10.1007/s10854-021-06760-2

Abstract:CoAl2O4 spinel ceramics were prepared via a standard solid-state reaction method, and their crystal structure, microwave dielectric properties, and dielectric resonant antenna applications were systematically investigated in this study. X-Ray diffraction patterns and Raman spectra confirmed that CoAl2O4 belongs to the Fd-3 m space group with cubic crystal symmetry. εr and Qf values increased with the increasing sintering temperature, where an ever-improving microstructure was also observed from the scanning electron micrographs. The optimal microwave dielectric properties were achieved as follows: εr = 9.34, Qf = 30,500 GHz, and τf = -54 ppm/°C. Moreover, a dielectric resonant antenna was designed and simulated to demonstrate the application prospects of CoAl2O4 ceramics towards microwave antennas. The CoAl2O4-based antenna resonating at 14.33 GHz exhibited a high return loss of -40.9 dB, a wide impedance bandwidth of 940 MHz, and an exceptionally high total efficiency of 96.6%. The remarkable antenna performances suggested that CoAl2O4 ceramics were promising candidates for wireless communication devices operating at the Ku-band, provided τf can be further tuned toward zero.