Chemical stability, morphological behavior of Mg/Sr-hydroxyapatite@chitosan biocomposites for medical applications
M. Afifi,Mehrez E. El-Naggar,Shabbir Muhammad,Noweir Ahmad Alghamdi,S. Wageh,M.A. Abu-Saied,M.A. El-Morsy,Waheed M. Salem,Mervat S. Mostafa,Salem R. Salem
DOI: https://doi.org/10.1016/j.jmrt.2022.02.107
IF: 6.267
2022-05-01
Journal of Materials Research and Technology
Abstract:Long-term biocompatible scaffolds based on chitosan (CS) encapsulated with hydroxyapatite (HAP) have been developed for orthopedic applications. The biocomposites consisting of magnesium (Mg)/strontium (Sr) co-dopant into were fabricated using a casting technique, whereas Mg(II) contribution was varied. The crystal growth seems to be in the c-axis upon the rising of Mg(II) content, whereas the c/a ratio changed from 0.72 to 0.73. Moreover, it was suggested that Mg(II) ions prefer to substitute Ca(1) rather than Ca(2) sites within HAP crystals. The investigation of surface morphology indicated that the Mg/Sr-HAP was formed as agglomerated grains with dimensions around 5.1-9.2, 6.2-11.4, 3.6-7.3, 3.1-18.3, and 6.1-18.3 μm, while the grains of CS were developed as 4.6-7.6, 3-14.3, 2.4-6.1, 9.1-30.5 and 6.2-9.1 μm for 0.0Mg/, 0.2Mg/, 0.4Mg/, 0.6Mg/, and 0.8Mg/, respectively. Moreover, the roughness average (Ra) increased from 37.3 to 48.4 nm for the lowest and the highest additional Mg(II). Furthermore, the compressive strength was investigated and exhibited that Mg(II) has induced high resistance to fracture, whereas compressive strength increased from 7.17±1.1 to 15.1±1.5 MPa for the highest Mg(II). The cell viability also was tested, and the high value (105.2±6.8 %) was achieved for the highest Mg(II). Finally, the corrosion behavior for the scaffolds through simulated body fluids was investigated and illustrated that the corrosion potential (ECorr) was shifted to positive values from -0.14 to -0.002 V upon the variation of Mg(II) contrition.
materials science, multidisciplinary,metallurgy & metallurgical engineering