Abstract:PtCu alloy nanocrystals, especially for the PtCu3 component, hold great potential as catalysts in methanol oxidation reaction (MOR) owing to their promising catalytic properties arising from the bifunctional mechanism associated with Pt and Cu sites. However, Pt and Cu salt precursors are difficult to be co-reduced in a synthesis due to the large difference in their redox potential, because of which Pt or Cu nanocrystals are initially generated and then evolve into a PtCu alloy with remarkable variation of the PtCu component by underpotential deposition (UPD) and galvanic replacement, respectively. Here we report a facile method for the shape-controlled synthesis of PtCu3 alloy nanocrystals by co-reduction of Pt and Cu salt precursors using oleylamine (OAm) and N,N-dimethylformamide (DMF) as co-reducing agents at different temperatures. PtCu3 alloy hexapods with preferential overgrowth along the <100> direction are obtained at 220 degrees C through co-reduction reaction accompanied by Cl- ion induced underpotential deposition (UPD). Meanwhile, galvanic replacement between PtCu3 alloy nanocrystals and the Pt precursor co-exists with overgrowth induced by co-reduction reaction at 190 degrees C, eventually resulting in PtCu3 hollow nanoframes. Both the PtCu3 alloy hexapods and hollow nanoframes exhibit remarkably enhanced catalytic properties in terms of activity and stability towards MOR relative to the commercial Pt/C. Specifically, the PtCu3 alloy hexapods and hollow nanoframes show the highest specific (2.96 mA cm(-2)) activity and mass activity (1.861 mA mu g(Pt)(-1)) for MOR, respectively, which are 13.5 and 24.2 times higher than those of the commercial Pt/C. This enhancement can be attributed to their unique structures and the possible bifunctional mechanism between Pt and Cu.

Low-Pt Octahedral PtCuCo Nanoalloys: "One Stone, Four Birds" for Oxygen Reduction and Methanol Oxidation Reactions

Local Coordination and Ordering Engineering to Design Efficient Core-Shell Oxygen Reduction Catalysts

Composition-driven Shape Evolution to Cu-rich PtCu Octahedral Alloy Nanocrystals As Superior Bifunctional Catalysts for Methanol Oxidation and Oxygen Reduction Reaction

Facile Synthesis of PtCu3alloy Hexapods and Hollow Nanoframes As Highly Active Electrocatalysts for Methanol Oxidation

Multicomponent Platinum-Free Nanoporous Pd-based Alloy As an Active and Methanol-Tolerant Electrocatalyst for the Oxygen Reduction Reaction

Enhancing oxygen reduction reaction of Pt–Co/C nanocatalysts via synergetic effect between Pt and Co prepared by one-pot synthesis

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

MOF Templated Nitrogen Doped Carbon Stabilized Pt–Co Bimetallic Nanoparticles: Low Pt Content and Robust Activity Toward Electrocatalytic Oxygen Reduction Reaction

Monodispersed Sub-5.0 Nm PtCu Nanoalloys As Enhanced Bifunctional Electrocatalysts for Oxygen Reduction Reaction and Ethanol Oxidation Reaction

An Alternate Aqueous Phase Synthesis of the Pt3Co/C Catalyst Towards Efficient Oxygen Reduction Reaction

Synergistic Bimetallic Metallic Organic Framework-Derived Pt-Co Oxygen Reduction Electrocatalysts

Electronegativity- induced cobalt-doped platinum hollow nanospheres with high CO tolerance for efficient methanol oxidation reaction

Collaborative Anchoring of Pt Nanoparticles and Metal Oxide Nanoparticles on N-Doped Carbon as Catalysts for Oxygen Reduction

Pt–Au–Co Alloy Electrocatalysts Demonstrating Enhanced Activity and Durability toward the Oxygen Reduction Reaction

Octahedral PtNi nanoparticle catalysts: exceptional oxygen reduction activity by tuning the alloy particle surface composition.

Octahedral Pd@Pt1.8Ni Core-Shell Nanocrystals with Ultrathin PtNi Alloy Shells As Active Catalysts for Oxygen Reduction Reaction.

Optimized oxygen reduction activity by tuning shell component in Pd@Pt-based core-shell electrocatalysts

Pt/C–LiCoO2 composites with ultralow Pt loadings as synergistic bifunctional electrocatalysts for oxygen reduction and evolution reactions

Pt-Fe-Co Ternary Metal Single Atom Catalyst for toward High Efficiency Alkaline Oxygen Reduction Reaction

Enhancing Electrocatalytic Methanol Oxidation on PtCuNi Core–Shell Alloy Structures in Acid Electrolytes

Catalytic Performance and Mechanism of N-Coti@Cotio3 Catalysts for Oxygen Reduction Reaction