Incorporation of Silver-Embedded Carbon Nanotubes Coated with Tannic Acid into Polyamide Reverse Osmosis Membranes toward High Permeability, Antifouling, and Antibacterial Properties
Afang Zhao,Na Zhang,Qiang Li,Lianwen Zhou,Huining Deng,Zhenghua Li,Yi Wang,Enguang Lv,Zhen Li,Mei Qiao,Jihua Wang
DOI: https://doi.org/10.1021/acssuschemeng.1c03313
2021-08-16
Abstract:In this work, tannic acid (TA)-functionalized carbon nanotubes () were synthesized by hydrogen bond and π–π stacking interactions. embedded with silver nanoparticles () was obtained by in situ reducing silver ammonia ions in the pore channels of and were added into the polyamide (PA) layer by interfacial polymerization to fabricate high-performance nanocomposite reverse osmosis membranes. The results show that the functionalized CNTs can be uniformly distributed in the PA matrix with random orientations. A loose PA separation layer was obtained by introducing Correspondingly, abundant new water channels were formed. Compared with the pure PA membrane, the water permeability (4.81 L m–2 h–1 bar–1) of the nanocomposite membrane is enhanced by 49.8% without any loss in NaCl rejection (99.3%). The membrane exhibits satisfactory chemical- and bio-fouling resistances to bovine serum albumin and Escherichia coli as model foulants. The high bactericidal rate should be ascribed to the formation of the TA coating and confined Ag nanoparticles in CNT channels. The confined structure effectively avoids the leaching out of the Ag nanoparticles and keeps the persistence of the antibacterial property. The excellent compatibility between the CNTs and the polyamide matrix endows the membrane with long-term performance stability.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c03313.Experimental procedure of the antibacterial property of the membranes; optical photographs of the uncoated CNT, , and samples dispersed in deionized water; EDX spectrum of the sample; three-dimensional AFM and SEM images of the fabricated various membranes; permeate fluxes and salt rejections of the PA/ membranes with different amounts of the incorporated in 2% MPD solution; formed bacterial colonies by 24 h growth on the agar culture medium after E. coli suspension contacting with the fabricated various membranes; arithmetic average value (Ra) and root-mean-square value (Rq) of the membrane surface roughness from AFM measurements; flux decline rate (Fdr), flux recovery rate (Frr), and irreversible decline rate (Firr) in each fouling cycle for the fabricated PA-based membranes using 100 mg/L BSA as a foulant solution; resistance values from the concentration polarization (rcp) and the reversible (rrf) and irreversible (rif) fouling resistance values of the fabricated PA-based membranes, respectively, using 100 mg/L BSA and 10 mg/L HA as foulant solutions (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology