Abstract:In this study, the growth behavior of Indium gallium nitride (InGaN)-based nanocolumn arrays was investigated, and red emission nanocolumn micro-light emitting diodes (μ-LEDs) were fabricated. The internal structure of the InGaN/GaN superlattice (SL) layer under the multiple-quantum-well (MQW) active layers was evaluated using scanning transmission electron microscopy (STEM) analysis. It was revealed that the InGaN crystal plane at the top of the nanocolumn changed from the c-plane, (1-102) plane, to the (10-11) plane as the number of SL pairs increased. A semipolar (10-11) plane was completely formed on top of the nanocolumn by growing InGaN/GaN SLs over 15-20 pairs, where the InGaN/GaN SL layers were uniformly piled up, maintaining the (10-11) plane. Therefore, when InGaN/AlGaN MQWs were grown on the (10-11) plane InGaN/GaN SL layer, the growth of the (10-11) plane semipolar InGaN active layers was observed in the high-angle annular dark field (HAADF)-STEM image. Moreover, the acute nanocolumn top of the (10-11) plane of the InGaN/GaN SL underlayer did not contribute to the formation of the c-plane InGaN core region. Red nanocolumnμ-LEDs with anφ12μm emission window were fabricated using the (10-11) plane MQWs to obtain the external quantum efficiency of 1.01% at 51 A cm-2. The process of nanocolumnμ-LEDs suitable for the smaller emission windows was provided, where the flat p-GaN contact layer contributed to forming a fine emission window ofφ5μm.

Red InGaN nanowire LED with bulk active region directly grown on p-Si (111)

Achieving InGaN-Based Red Light-Emitting Diodes by Increasing the Growth Pressure of Quantum Wells

Demonstration of 621-Nm-wavelength InGaN-based Single-Quantum-well LEDs with an External Quantum Efficiency of 4.3% at 10.1 A/cm2

Red light-emitting diode with full InGaN structure on ScAlMgO 4 substrate

Single nanowire green InGaN/GaN light emitting diodes.

Understanding the p-Type GaN Nanocrystals on InGaN Nanowire Heterostructures

InGaN-Based microLED Devices Approaching 1% EQE with Red 609 nm Electroluminescence on Semi-Relaxed Substrates

InGaN/GaN superlattice underlayer for fabricating of red nanocolumn μ-LEDs with (10-11) plane InGaN/AlGaN MQWs

Ingan/Gan Blue Light Emitting Diodes Grown on Si(110) and Si(111) Substrates

Improving Performances of Ultra-Small Size (1–20 Μ M) InGaN Red Micro-Leds by Growing on Freestanding GaN Substrates

InGaN/GaN multi-quantum-well nanowires and light emitting

Efficient InGaN-based Red Light-Emitting Diodes by Modulating Trench Defects

Demonstration of Low Forward Voltage InGaN-based Red LEDs

Wafer-scale emission uniformity of InGaN-based red light-emitting diodes on an in situ InGaN decomposition template

GaN-Based LEDs Grown on Graphene-Covered SiO2/Si (100) Substrate

High efficiency InGaN nanowire tunnel junction green micro-LEDs

Semipolar ( 11̅01 ) InGaN/GaN red–amber–yellow light-emitting diodes on triangular-striped Si (100) substrate

Evidence of two-dimensional lateral quantum confinement in self-formed core–shell InGaN nanowires on Si (111) emitting in the red

Engineering the Carrier Dynamics of InGaN Nanowire White Light-Emitting Diodes by Distributed p -AlGaN Electron Blocking Layers

Demonstration of 651?nm InGaN-based red light-emitting diode with an external quantum efficiency over 6% by InGaN/AlN strain release interlayer

High-color-rendering-index Phosphor-Free InGaN-based White Light-Emitting Diodes by Carrier Injection Enhancement Via V-pits