Preparation and Evaluation of Co-Doped Fe7S8/C Composites for Lithium Storage

Tingting Huang,Zhaoxiu Xu,Suqin Wang,Jiamin Xu,Qiaoyu Liang,Hongbo Li

DOI: https://doi.org/10.1021/acs.inorgchem.3c00430

2023-05-15

Abstract:Fe7S8 has a high theoretical capacity (663 mAh g-1) and can be prepared at a low cost, making it advantageous for production. However, Fe7S8 has two disadvantages as a lithium-ion battery anode material. The first is that the conductivity of Fe7S8 is not good. The second is that when the lithium ion is embedded, the volume expansion of the Fe7S8 electrode is serious. That is why Fe7S8 has not been used in real life yet. In this paper, Co-Fe7S8/C composites were prepared by doping Co into Fe7S8 through a one-pot simple hydrothermal method. In situ Co is doped into Fe7S8 to produce a more disordered microstructure to improve ion and electron transport performance, thereby reducing the activation barrier of the main material. The Co-Fe7S8/C electrode presents a high specific discharge capacity of 1586 mAh g-1 and a Coulombic efficiency (CE) of 71.34% at an initial cycle at 0.1 A g-1. After 1500 cycles, the specific discharge capacity remains at 436 mAh g-1 (5 A g-1). When the current density returns to 0.1 A g-1, the capacity almost returns to the initial level, showing excellent rate performance.