Trisodium phosphate-loaded magnesium‐aluminum layered double hydroxides/oxidized-multiwalled carbon nanotubes self-assembled 2D-nanohybrid for designing a multifunctional smart epoxy nanocomposite
Saeede Rezaeifard,Taghi Shahrabi,Bahram Ramezanzadeh
DOI: https://doi.org/10.1016/j.clay.2024.107376
IF: 5.907
2024-04-25
Applied Clay Science
Abstract:In this study, a hybrid nanomaterial based on layered double hydroxides (LDH) and multi-walled carbon nanotubes (MWCN) was fabricated using a co-precipitation method. Trisodium phosphate (TP) was loaded into the designed nanocarrier to enhance the corrosion resistance of mild steel in 3.5 wt% NaCl media. Fourier transform infrared (FT-IR) spectroscopy, Raman, and X-ray diffraction (XRD) analyses were carried out to investigate the magnesium‐aluminum layered double hydroxides/oxidized-multiwalled carbon nanotubes (Mg-AL-LDH/O-MWCN) structure and morphology before and after loading of trisodium phosphate. Furthermore, the nanocarrier inhibition capability was evaluated through electrochemical impedance spectroscopy (EIS), polarization, and field emission-scanning electron microscopy (FE-SEM) techniques. Electrochemical impedance spectroscopy (EIS) was also employed to estimate the anticorrosion properties of the epoxy coating loaded with TP-LDH/O-MWCN. The EIS evaluation of the intact coating revealed the impedance at the lowest frequency (|Z| 0.01 Hz ) of about 10 9 Ω.cm 2 after 42 days of immersion for the trisodium phosphate-layered double hydroxides/oxidized-multi-walled carbon nanotubes@epoxy (TP-LDH/O-MWCN@EP) sample and the lowest value of breakpoint frequency was obtained for this sample (f b = 0.063 Hz). These findings prove the trisodium phosphate-layered double hydroxides/oxidized-multi-walled carbon nanotubes (TP-LDH/O-MWCN) particles' effectiveness in the epoxy coating water/ion barrier function enhancement. EIS results indicated the enhancement of the charge transfer resistance (R ct ) of the scratched coatings, from 65.97 kΩ.cm 2 for the pure epoxy (EP) sample to 94.87 kΩ.cm 2 for the trisodium phosphate-layered double hydroxides/oxidized-multi-walled carbon nanotubes@epoxy (TP-LDH/O-MWCN@EP) sample, revealing the self-repairing behavior of the designed coating. In addition, the adhesion properties of the samples coated with LDH/O-MWCN@EP and TP-LDH/O-MWCN@EP were studied by pull-off and cathodic disbonding tests, leading to a 33% reduction in adhesion loss and a 52.23% reduction in the diameter of cathodic delamination. The tensile test conducted on the samples indicated an increase in the ultimate tensile strength (σ UTS ), elongation break (Ɛ b ), and toughness values by 188%, 223%, and 800%, respectively, in comparison with the pure epoxy (EP) sample.
mineralogy,chemistry, physical,materials science, multidisciplinary