Photosensitizing activity of phthalocyanine derivatives dispersed on nanostructured amberlyst 15: Free base vs . metal complexes

Nasrin Ghanbari,Saeed Zakavi

DOI: https://doi.org/10.1016/j.dyepig.2024.111999

IF: 5.122

2024-02-04

Dyes and Pigments

Abstract:A major problem with the use of peripherally unsubstituted metal-free phthalocyanine (H 2 Pc) and the corresponding metal complexes with Co(II), Zn(II) and Ni(II) as catalysts or photocatalyts is their extensive aggregation in most organic solvents and water. In order to overcome the aggregation of phthalocyanine compounds, metal-free phthalocyanine (H 2 Pc) and the corresponding metal complexes with Co(II), Zn(II) and Ni(II) dispersed on porous nano-structured amberlyst 15 (nanoAmbSO 3 H) were synthesized and used as efficient photosensitizers in the aerobic oxidation of methyl phenyl sulfide under aqueous and non-aqueous conditions. The polymer supported photosensitizers, H 2 Pc@nanoAmbSO 3 H, ZnPc@nanoAmbSO 3 H, CoPc@nanoAmbSO 3 H and NiPc@nanoAmbSO 3 H , were characterized by diffuse reflectance UV–Vis spectroscopy (DRS), FESEM/EDX-Mapping, AFM, IR, TGA and BET. The singlet oxygen quantum yield (φ Δ ) of the photosensitizers was determined through the oxidation of 1,3-diphenylisobenzofuran as a specific quencher of singlet oxygen. Solution UV–vis and DRS studies showed the lack of metal leaching from the metal complexes but significant red shift of the absorption bands upon exposure to sulfuric acid and the acidic conditions caused by the –SO 3 H groups of the strongly acidic polymer. A particle size less than 50 nm was determined for the almost spherical nanocomposites. In contrast to the metallophthalocyanines, the incorporation of H 2 Pc into the polymer structure led to a remarkable decrease in the thermal stability of the polymer. The immobilized photosensitizers were much more efficient than the non-immobilized counterparts (CoPc, ZnPc, NiPc and H 2 Pc), although no catalyst degradation was observed for the both series.

engineering, chemical,chemistry, applied,materials science, textiles