PREPARATION AND PROPERTIES OF A NOVEL THERMOSENSITIVE POLYMER CONTAINING COBALT PHTHALOCYANINE
Feng Guihua,Shen Xiaoyuan,Li Nan,Zhao Baoyan,Yao Yuyuan,Lue Wangyang,Chen Wenxing
DOI: https://doi.org/10.3724/sp.j.1105.2008.00567
2008-01-01
Abstract:Metallophthalocyanine has attracted considerable attention as oxidation catalyst :because its structure similar to the active center of cytochrome P-450, and it can promote many reactions through oxidase-like, catalase-like, as well as peroxidase-like mechanism, whereas it has the following problems: low solubility, high aggregation tendency, difficulty in catalyst recovery and recycling, which restrict its further application as catalyst. Poly ( Niso propylacrylamide) (PNIPAAm) is a typical thermosensitive polymer, and it can be homogeneous below its lower critical solution temperature ( LCST) and completely precipitated above LCST, which makes it become an attractive polymer support for catalyst. A novel reactive and aqueous soluble metallophthalocyanine derivative, cobalt tetra(2,4dichloro- 1, 3, 5-triazine) aminophthalocyanine (Co-TDTAPc was synthesized by the modification of cobalt aminophthalocyanine with 2,4,6-trichloro-1,3,5-triazine and immobilized on PNIPAAm by covalent bond to obtain a thermosensitive polymer catalyst, PNIPAAm-g-Co-TDTAPc. The polymer catalyst was characterized by UV-Vis spectrometer in ethanol and THF, and the results showed that PNIPAAm-g-Co-TDTAPc had characteristic absorption peaks of cobalt phthalocyanine (13 band: 280 similar to 330 nm; Q band: 620 similar to 700 nm) in both ethanol and THF, while PNIPAAm had no absorption in these area, which proved that the Co-TDTAPc had been successfully grafted on PNIPAAm. The thermal stability of the polymers were also tested by heating from room temperature to 600 degrees C at a rate of 20 K/min in a nitrogen environment with flow rate of 100 mL/min. The results indicated that the beginning decomposition temperature of PNIPAAm-g-Co-TDTAPc was 407 degrees C which confirmed that the polymer catalyst had high thermal stability. The solubility of small molecular cobalt phthalocyanine, PNIPAAm and PNIPAAm-g-CoTDTAPc was investigated in different solvents. The results showed that PNIPAAm-g-Co-TDTAPc could dissolve in water and most organic solvents, while the small molecule cobalt plithaloyanine only dissolve in DMSO and DMF, which proved that the solubility of cobalt phthalocyanine was improved significantly after immobilization on PNIPAAm. The thermosensitive property of PNIPAAm-g-Co-TDTAPc was investigated by cloud point measurements, and the results showed that PNIPAAm-g-Co-TDTAPc exhibited excellent thermosensitive property in aqueous solutions, and its LCST was 34.5C. The LCST of PNIPAAm-g-Co-TDTAPc in the mixture of water and organic solvents (ethanol and DMF) was also studied, and the experimental results showed that the LCST of PNIPAAm-gCo-TDTAPc first decreased when the volume fraction of ethanol in mixed solvents increased below 27.5% and then sharply increased above 59.5% until the thermosensitivity of PNIPAAm-g-Co-TDTAPc disappeared. The experimental results in DMF/water mixed solvents were similar to those in water/ethanol. Furthermore, the catalytic activity of PNIPAAm-g-Co-TDTAPc on 2-mercaptoethanol was investigated by the consumption of oxygen at different temperature and pH 11 The results indicated that PNIPAAm-g-Co-TDTAPc had a high catalytic oxidation activity on 2-mercaptoethanol, and the reaction rate was first increased with the temperature increasing and then rapidly decreased when temperature was over LCST due to the precipitation of this catalyst from the solution. In conclusion, a novel high efficient polymer catalyst was prepared, which has both good solubility and excellent thermosensitive properties.Based on the above properties, it can be served as a hoogeneous catalyst and separated just by heating, having potential applications in the fields of organic synthesis and degradation of organic pollutants.