Abstract:Purpose: Mechanical properties of dental composite resins need to be improved in order to enhance their performance for applications in direct restorations. Application of nanoparticles in this field is a recent development. The aim of this study was to investigate the mechanical properties of experimental composites containing various mass fractions of silica nanoparticles. Materials and methods: Experimental composites were composed of a visible-light-curing monomer mixture (70 wt% Bis-GMA and 30 wt% TEGDMA) and silica nanoparticles of a size ranging from 20 nm to 50 nm modified with gamma-methacryloxy propyl trimethoxy silane (gamma-MPS) as reinforcing filler. The composites were classified into four groups according to their filler mass fractions ranging from 20% to 50%. Following the same preparation procedure, a conventional composite was also fabricated consisting of a mass percentage of 60% silica fillers having particle sizes ranging from 10 microm to 40 microm in the same organic matrix, which served as control. Ten specimens were prepared of each experimental group and also of the control. Fracture toughness was measured using single-edge notched bend (SENB) specimens. Specimen fracture surfaces were mounted on aluminum stubs with carbon cement, sputter-coated with gold and examined under scanning electron microscopy (SEM). Flexural strength was evaluated through a standard three-point bending test and Vickers microhardness test was performed to investigate the hardness of the samples. Results: Filler mass fraction had a significant effect on composite properties. Fracture toughness, flexural strength, and hardness of composites at filler mass fraction of 40% of silica nanoparticles were (mean +/- SD) 1.43 +/- 0.08 MPa.m(1/2), 149.74 +/- 8.14 MPa, and 62.12 +/- 3.07 VHN, respectively; relevant values for composites at 50% mass fraction of silica nanoparticles were 1.38 +/- 0.07 MPa.m(1/2), 122.83 +/- 6.13 MPa, and 70.69 +/- 3.67 VHN, respectively, all of which were significantly higher than 1.07 +/- 0.06 MPa.m(1/2), 104.61 +/- 8.73 MPa, and 52.14 +/- 4.02 VHN of the control, respectively (Tukey's multiple comparison test; family confidence coefficient = 0.95). Measured values for composites at 20% mass fraction of silica nanoparticles were 0.94 +/- 0.06 MPa.m(1/2), 103.41 +/- 7.62 MPa, and 42.87 +/- 2.61 VHN, respectively; relevant values for composites at 30% mass fraction of silica nanoparticles were 1.16 +/- 0.07 MPa.m(1/2), 127.91 +/- 7.05 MPa, and 51.78 +/- 3.41 VHN, respectively. Conclusions: Reinforcement of dental composite resins with silica nanoparticles resulted in a significant increase in the evaluated mechanical properties in comparison with the conventional composite. The filler mass fraction played a critical role in determining the composite's mechanical properties.

The effect of Bioglass addition on mechanical and physical properties of photoactive UDMA-TEGDMA resin composites

The Effect of UDMA/TEGDMA Mixtures and Bioglass Incorporation on the Mechanical and Physical Properties of Resin and Resin‐Based Composite Materials

Effect of Silica Nanospheres Silanized by Functional Silanes on the Physicochemical and Mechanical Properties of Bis-GMA/TEGDMA Dental Composite Resin by Photocuring Synthesis

Investigation of mechanical properties of experimental Bis-GMA/TEGDMA dental composite resins containing various mass fractions of silica nanoparticles

Effect of Monodisperse Mesoporous Bioactive Glass Spheres (mbgs) on the Mechanical Properties and Bioactivity of Dental Composites

Effect of barium silicate on mechanical properties, transmittance, and protein adsorption of resin for additive manufacturing containing zwitterionic polymer

The Physiochemical Properties of Dental Resin Composites Reinforced with Milled E-glass Fibers

Bis-EMA/Bis-GMA ratio effects on resin-properties and impregnated fiber-bundles

The researchment of nami-material reinfoced dental composite resin

Effect of adding ytterbium trifluoride filler particles on the mechanical, physicochemical and biological properties of methacrylate-based experimental resins for 3D printing

Biomechanical and Biological Evaluations of Novel BPA-free Fibre-Reinforced Composites for Biomedical Applications

Mechanical and Dynamic Properties of Resin Blend and Composite Systems: A Molecular Dynamics Study

Effect of Bioactive Filler Addition on the Mechanical and Biological Properties of Resin-Modified Glass Ionomer

Polymerization and shrinkage kinetics and fracture toughness of bulk-fill resin-composites

Study on the Polymerization Shrinkage and Mechanical-Physical Properties of Dental Resin Composite Modified by Polyurethane Dimechacrylate and Glass Flake Fillers

Effect of post-curing treatment on mechanical properties of composite resins

Preparation and characterization of acrylic resins with bioactive glasses

Effect of E-glass fibers addition on compressive strength, flexural strength, hardness, and solubility of glass ionomer based cement

Formulation, Configuration, and Physical Properties of Dental Composite Resin Containing a Novel 2π + 2π Photodimerized Crosslinker - Cinnamyl Methacrylate: An In Vitro Research

Bioactivity and Physico-Chemical Properties of Dental Composites Functionalized with Nano- vs. Micro-Sized Bioactive Glass

Surface grafting of Poly (ether ether ketone) on silica particles as novel filler for dental composites: Physico-chemical characterization