Comparative Studies Between Surface and Bulk Structural Changes During Heating and Cycling for Layer-Structured and Olivine-Structured Cathode Materials
Kyung-Wan Nam,Xiao-Qing Yang,Xiaojian Wang,Yongning Zhou,Hung-Sui Lee,Lijun Wu,Yimei Zhu,Hong Li,Xuejie Huang,Liquan Chen
DOI: https://doi.org/10.1149/ma2010-03/1/318
2010-01-01
ECS Meeting Abstracts
Abstract:Layer structured oxides with transition metals such as Ni, Co, and Mn have been considered as good cathode materials to replace LiCoO2 for lithium batteries due to their lower cost and higher capacity. The thermal instability in charged, especially over charged states at elevated temperatures, however, is still a major concern on this class of materials. Recently, we have developed a technique using the combination of a high intensity synchrotron x-ray beam and a fast image plate detector to do time resolved x-ray diffraction during the thermal decomposition of charged cathode materials in the presence of electrolyte. In order to understand the controlling mechanism of thermal runaway of the electrodes in Li-ion cells, we have monitored structural changes of the charged nickel-based cathode materials in the presence of electrolyte. We have also developed synchrotron based in situ and ex situ soft x-ray absorption spectroscopy (XAS) techniques which allows us to distinguish the structural differences between surface and bulk of electrodes using both electron yield (EY) and fluorescence yield (FY) detectors simultaneously. In this presentation, we will report our studies on the structural changes of cathode materials during heating with and without the presence of the electrolytes, as well as the structural differences between the surface and the bulk during heating. Our recent studies on Co, Al, Mn doped LiNiO2-based materials using time-resolved X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS) with or without the presence of electrolyte show a series of phase transformations during heating [1]. However, due to the averaging nature of X-ray techniques, detailed information about how the structure changes initiated and propagated through new phase nucleation and growth in the microscopic level is quite limited. Therefore further studies using a local probe with high spatial resolution are needed. Here, we present our insitu transmission electron microscopy (TEM) studies on the structural changes of over charged Li0.0Ni0.8Co0.15Al0.05O2 and Li0.0Ni1/3Co1/3Mn1/3O cathode materials during heating, in comparison with our XRD and XAS studies. High resolution transmission electron microscopy (HRTEM) and electron diffraction were carried out using JEM-3000F equipped with an ultra high resolution (UHR) objective-lens pole-piece, an offaxis 1024 x 1024 Gatan slow-scan camera, a post column Gatan imaging filter (GIF), a NORAN X-ray detector, and a Gatan double-tilt heating stage capable with temperature ranging from room temperature to 1000 oC. The Li0.0Ni0.8Co0.15Al0.05O2 particles harvested from overcharged cell were first examined at room temperature. Electron diffraction and HRTEM show that the main phase is a layered structure with rhombohedral symmetry. Interestingly, rock-salt structure and spinel structure, which only observed at elevated temperatures using X-ray techniques, were presented at the edges and thin areas of the particles, respectively even at room temperature. This implies that after overcharging, the particles start losing some oxygen atoms near the particle surface, resulting in the structural changes. By heating the sample, we observed that the phase with the spinel structure nucleates and grows more and more into the thick area of the particles, while the rock-salt phase propagates from the surface to the interior of the particles. After heating the sample to 400 oC, the structure of the whole sample completely transformed to the rock-salt structure. For the over-charged Li0.0Ni1/3Co1/3Mn1/3O2 sample, spinel structure was also observed on the surfaces of the particles at room temperature. The olivine-structured LiFePO4 and LiFeMPO4 (M=Mn, Co, Ni) solid solution type cathode materials have been studied intensively recently [2-8], due to their high thermal and electrochemical stabilities and good safety characteristics. The in depth understanding of the structural changes during charge-discharge cycles will provide guidance for developing new materials. Using synchrotron based in situ XRD, hard and soft x-ray XAS, and TEM, the structural changes of these materials have been studied during chargedischarge cycling. The differences of phase transition processes between the surface and the bulk will be discussed.