Highly conductive and dimensionally stable anion exchange membranes enabled by rigid poly(arylene alkylene) backbones
Tao Wang,Yu Zhao,Ruoxi Ma,Lijuan Li,Qianjun Ling,Xueliang Li,Yunsheng Ding,Haibing Wei
DOI: https://doi.org/10.1016/j.synthmet.2023.117385
IF: 4
2023-05-31
Synthetic Metals
Abstract:Dimensionally and chemically stable anion exchange membranes with excellent ion conductivity are highly desired in electrochemical energy conversion technologies. Herein, we present a design using rigid arylene units, i.e., p -tetraphenylene and p -terphenylene, to suppress the water sorption of quaternized poly(arylene alkylene) membranes with high ion contents. Of note, side chain double-quaternary ammonium (QA) functionalized poly( q -tetraphenylene- co - p -terphenylene alkylene) membrane P(4PA- co -3PA)-D100 with the IEC value as high as 2.93 mmol g −1 showed very limited water uptake and swelling at 80 °C of 75 wt% and 14 %, respectively. Meanwhile, the immiscibility of hydrophilic double-cation side chain and the hydrophobic poly(arylene alkylene) backbone drives the formation of phase-separated morphology. As a result, P(4PA- co -3PA)-D100 showed an exceptional conductivity of 227.8 mS cm −1 at 80 °C with activation energy of 10.5 kJ mol −1 . Despite the rigid poly(arylene alkylene) backbone with highly chemical durability and oxidative stability, the tandem tethered double cation in the side chain showed a 11 % QA moiety loss after a 1000-h treatment in 2 M NaOH at 80 °C. Moreover, a good peak power density of 550 mW cm −2 at the current density of 1.06 A cm −2 was achieved for P(4PA- co -3PA)-D100 with the gases flow of 200 mL min −1 . This work demonstrates that, in addition to the approach of cross-linking, the highly conductive AEMs with excellent dimensional stability can be achieved by improving the rigidity of polymer backbones.
materials science, multidisciplinary,physics, condensed matter,polymer science