Facile preparation of isocyanate-functionalized poly(styrene- co -maleimide- co -maleic anhydride) particle and its application as a versatile support for nano-sized TiO 2 photocatalyst
Liu Yang,Yingxue Wu,Hongyi Shu,Chuang Wang,Changetong Song,Xianhong Zhang,Dong Chen,Yuhong Ma,Wantai Yang
DOI: https://doi.org/10.1016/j.apsusc.2023.157536
IF: 6.7
2023-05-19
Applied Surface Science
Abstract:Polymer-supported catalysts have attracted intensive research attentions due to easy handling, facile separation and outstanding recycling performance. Herein, a simple, efficient and universal strategy was developed to fabricate isocyanate-functionalized polymer microspheres bearing highly reactive surface isocyanate groups, which could serve as a versatile support for the immobilization of photocatalyst. Firstly, self-stabilized precipitation polymerization of maleimide, maleic anhydride and styrene was performed in the presence of divinyl benzene (crosslinker) to prepare imide-functionalized poly(styrene- co -maleimide- co -maleic anhydride) (PSMM) microspheres. By simply adjusting the solvent composition and monomer feed ratio, monodisperse PSMM particles with diameter in the range of 0.52-1.01 μm were successfully obtained, which were further modified with hexamethylene diisocyanate (HDI). As a proof-of-concept, TiO 2 nanoparticles were readily and covalently bound to the surface of HDI-functionalized PSMM (PSMM-HDI) particles through reaction with isocyanate groups, leading to the formation of PSMM-HDI supported TiO 2 ( 2 ). Furthermore, anhydride groups on the surface of PSMM was hydrolyzed to endow 2 with better dispersibility and adsorption performance. The degradation of methylene blue under UV-light was performed to evaluate the photocatalytic performance of the resultant 2 . Compared with pristine TiO 2 , the 2 exhibited not only higher degradation efficiency, but also facile separation and better reusability.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films