Revealing Exciton and Metal–Ligand Conduction Band Charge Transfer Absorption Spectra in Cu-Zn-In-S Nanocrystals
Brener R. C. Vale,Etienne Socie,Leticia R. C. Cunha,Andre F. V. Fonseca,Roberto Vaz,Jefferson Bettini,Jacques-E. Moser,Marco A. Schiavon
DOI: https://doi.org/10.1021/acs.jpcc.0c09681
2020-12-02
The Journal of Physical Chemistry C
Abstract:Copper indium sulfide quantum dots (QDs) have attracted substantial attention in recent years due to environmental issues and diverse applications. We report the synthesis and characterization of copper-zinc-indium-sulfide (CZIS) QDs and CZIS treated with excess Zn<sup>2+</sup> at different temperatures, denoted here as CZIS/ZnS 100 and CZIS/ZnS 200. Zn<sup>2+</sup> can diffuse into the lattice by an exchange-cation reaction, replacing Cu<sup>+</sup> and In<sup>3+</sup>. We employed transient absorption (TA) spectroscopy to study the role of Zn<sup>2+</sup> in the lattice. The data were treated by global analysis, which yielded the decay-associated spectra (DAS). Through DAS and second-order derivative absorption spectra, we could for the first time isolate the excitonic contribution from the metal–ligand conduction band charge transfer (ML<sub>CB</sub>CT) absorption in the TA spectrum, finding the hole localization lifetime by its spectral and dynamical features. The hole localization lifetime increases from 0.3 to 1.7 ps by increasing the Zn<sup>2+</sup> concentration. We also measured the electron-trapping constants to be dozens of picoseconds and nonradiative recombination larger than 1 ns. Finally, we concluded that suppression of the electron-trapping rate is not the only process responsible for increasing the photoluminescence quantum yield (PLQY); however, suppression of this process is important since it is the first step of the nonradiative recombination pathway. The detailed mechanism was proposed, and our results suggest that the introduction of Zn<sup>2+</sup> in the lattice of copper indium sulfide (CIS) QDs could be beneficial for charge extraction.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.jpcc.0c09681?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.jpcc.0c09681</a>.Global analysis; absorption cross-section measurements; PL maximum and second-order derivative absorption minimum; TA bleach minimum and true Stokes shift; dependence of TA bleaching on the photon fluence; estimated absorption cross-section wavelength dependence; TA spectra normalized at 1 ps and GSB decay at different photon fluences; decay curves probed at different energies; DAS pumped at 500 nm; time constants for DAS pumped at 500 and 390 nm; and PL decay curve obtained from TCSPC (<a class="ext-link" href="/doi/suppl/10.1021/acs.jpcc.0c09681/suppl_file/jp0c09681_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical,nanoscience & nanotechnology,materials science, multidisciplinary