Fe-MOF-Derived Efficient ORR/OER Bifunctional Electrocatalyst for Rechargeable Zinc–Air Batteries
Yun-Wu Li,Wen-Jie Zhang,Jing Li,Hui-Yan Ma,Hong-Mei Du,Da-Cheng Li,Su-Na Wang,Jin-Sheng Zhao,Jian-Min Dou,Liqiang Xu
DOI: https://doi.org/10.1021/acsami.0c11945
2020-09-09
Abstract:The construction of an efficient oxygen reduction reaction and oxygen evolution reaction (ORR/OER) bifunctional electrocatalyst is of great significance but still remains a giant challenge for high-performance metal–air batteries. In this study, uniform FeS/Fe<sub>3</sub>C nanoparticles embedded in a porous N,S-dual doped carbon honeycomb-like composite (<i>abbr.</i> FeS/Fe<sub>3</sub>) have been conveniently fabricated by pyrolysis of a single-crystal <b>Fe-MOF</b>, which has a low potential gap Δ<i>E</i> of ca. 0.72 V, a competitive power density of 90.9 mW/cm<sup>2</sup>, a specific capacity as high as 750 mAh/g<i><sub>Zn</sub></i>, and excellent cycling stabilities over 865 h (1730 cycles) at 2 mA/cm<sup>2</sup> when applied as a cathode material for rechargeable zinc–air batteries. In addition, the two series-linked Zn–air batteries successfully powered a 2.4 V LED light as a real power source. The efficient ORR/OER bifunctional electrocatalytic activity and long-term durability of the obtained composite might be attributed to the characteristic honeycomb-like porous structure with sufficient accessible active sites, the synergistic effect of FeS and Fe<sub>3</sub>C, and the N,S codoped porous carbon, which provides a promising application potential for portable electronic Zn–air battery related devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11945?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11945</a>.Material characterization, experimental details, electrochemical measurements, assembly of a Zn–air battery, structure and structure parameters of <b>Fe-MOF</b>, PXRD of <b>Fe-MOF</b>, SEM images, N<sub>2</sub> sorption isotherms, CV plots, and LSV curves of <b>Fe-MOF</b>-700, <b>Fe-MOF</b>-800, and <b>Fe-MOF</b>-1000, CV curves, K–L plots, and OER LSV curves of FeS/C, FE<sub>3</sub>C/C, and N,S-C catalysts, long-term cycling charge–discharge curve of the Pt/C + IrO<sub>2</sub> (1:1) benchmark, UV–vis spectra of <b>Fe-MOF</b>-900, crystal data and structure refinement parameters of the <b>Fe-MOF</b> precursor, and comparison of Zn–air battery performances from the literature (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11945/suppl_file/am0c11945_si_001.pdf">PDF</a>)Crystallographic data (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11945/suppl_file/am0c11945_si_002.cif">CIF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology