Abstract:Micropores and defects, like oxygen-containing groups, as active sites for sodium-ion storage in hard carbon have attracted considerable attention; nevertheless, most oxygen doping or oxidizing processes inevitably introduce undesired oxygen groups into a carbon framework, leading to deteriorated initial Coulombic efficiency (ICE). Here, precise carbonyl groups and closed micropores are together introduced into biomass-derived hard carbon to enhance the Na-ion storage performance. The hard carbon delivers a large reversible capacity of 354.6 mA h g–1 at 30 mA g–1, a high ICE (88.7%), as well as ultra-long cycling stability (277 mA h g–1 at 0.3 A g–1 over 1000 cycles; 243 mA h g–1 at 1 A g–1 over 5000 cycles). The rate capability and cycling stability of hard carbon in carbonate- and diglyme-based electrolytes are contrasted to demonstrate the superiority of diglyme. Cyclic voltammetry at varied scans and galvanostatic intermittent titration techniques are carried out to clarify the disparity between the two different electrolyte systems. Furthermore, the as-prepared hard carbon is utilized as the anode for sodium-ion full cells exhibiting an energy density of 166.2 W h kg–1 at 0.2 C and a long-cycle life (47.9% retention over 200 cycles at 1 C).The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c15884.Experimental details and materials for preparation of Na2FePO4 and energy density calculation methods for full cells; SEM images of pine and S-pine precursors, TEM images of PHC and TPHC, fitted SAXS patterns and models, structural parameter comparison, digital photos of the pine powder; CV curves of PHC-ester, TPHC-ester, S-TPHC-ester, and S-TPHC-ether, electrochemical performance comparison for various HC electrodes, charge–discharge curves for HC treated with various concentrations of H2SO4, ip–v correlations, and GITT curves for S-TPHC-ester and S-TPHC-ether; ex situ XPS results of the SEI for S-TPHC formed in ester and ether electrolytes; and electrochemical performance of Na2FePO4F/C half cells (PDF)This article has not yet been cited by other publications.

Peat-derived hard carbon electrodes with superior capacity for sodium-ion batteries

Biomass‐Derived Phosphorus‐Doped Porous Hard Carbon Anode for Stable and High‐Rate Sodium Ion Batteries

Curly hard carbon derived from pistachio shells as high-performance anode materials for sodium-ion batteries

A Life Cycle Assessment of Hard Carbon Anodes for Sodium-Ion Batteries

Realizing Improved Sodium-Ion Storage by Introducing Carbonyl Groups and Closed Micropores into a Biomass-Derived Hard Carbon Anode

Sulfur and phosphorus co-doped hard carbon derived from oak seeds enabled reversible sodium spheres filling and plating for ultra-stable sodium storage

Biomass hard carbon of high initial coulombic efficiency for sodium-ion batteries: Preparation and application

Pomegranate Peel-Derived Hard Carbons as Anode Materials for Sodium-Ion Batteries

From Natural Fibers to High-Performance Anodes: Sisal Hemp Derived Hard Carbon for Na-/K-Ion Batteries and Mechanism Exploration

Exploring Carbonization Temperature to Create Closed Pores for Hard Carbon As High-Performance Sodium-Ion Battery Anodes

Ultrahigh Plateau‐Capacity Sodium Storage by Plugging Open Pores

Biomass derived hard carbon used as a high performance anode material for sodium ion batteries

Sulfur-doping biomass based hard carbon as high performance anode material for sodium-ion batteries

Scalable synthesis of N/S co-doped hard carbon microspheres as a high-performance anode material for sodium-ion batteries

A porous biomass-derived anode for high-performance sodium-ion batteries

Optimizing Synthesis Temperature for Lignin-Derived Hard Carbon Anode for High Cycling Capacity in Sodium-Ion Batteries

Fabricating multi-porous carbon anode with remarkable initial coulombic efficiency and enhanced rate capability for sodium-ion batteries

Agar‐Derived Slope‐Dominated Carbon Anode with Puparium Like Nano‐Morphology for Cost‐Effective SIBs

Hard carbon anode derived from pre-treated bio-waste sugarcane bagasse for high capacity sodium-ion battery fabricated with bio-deFgradable porous polymer electrolyte

Porous hard carbon spheres derived from biomass for high-performance sodium/potassium-ion batteries

Lithium‐Pretreated Hard Carbon as High‐Performance Sodium‐Ion Battery Anodes