Abstract:Nitrous oxide (N2O) is a significant greenhouse gas and its emissions from fluidized bed combustion systems can be controlled using catalytic conversion and decomposition. The catalytic decomposition of N2O was studied in a quartz fixed-bed reactor at 450-700 degrees C. The low-cost catalyst was prepared from fly ash and iron oxides, and was characterized in terms of the BET specific surface area and XRD. This study showed that both the Fe content on the catalyst surface and the calcination temperature during the preparation of the catalyst should be optimized in order to significantly improve the catalyst performance when used for N2O decomposition. The influences of O-2, H2O, CO2 and SO2 on the N2O decomposition were investigated at the most reactive temperature. Experimental results showed that O-2 had a small negative effect on the catalytic activity, while CO2 had no obvious effect on the N2O decomposition. The N2O conversion was still high even when H2O was present. However, the N2O conversion dropped sharply when H2O and O-2 were both present. The catalytic activity was reduced by SO2 because of its reaction with the catalyst. The difference between the N2O conversion with H2O present and with both H2O and O-2 present was analyzed in order to determine the N2O decomposition mechanism. Two mechanisms for the N2O catalytic decomposition mechanism have been considered, of which the one with formation of oxygen atoms at two sites with migration and recombination shows better agreement with our experimental results. (C) 2009 Curtin University of Technology and John Wiley & Sons, Ltd.

Catalytic decomposition of N2O over Cu-Al-O x mixed metal oxides

Catalytic Decomposition of N2O over Cu-ZSM-11 Catalysts

Catalytic Decomposition of N2O over CuxCe1−xOy Mixed Oxides

Preparation of NiCe Mixed Oxides for Catalytic Decomposition of N2O

Catalytic Decomposition of N<SUB>2</SUB>O on Ordered Crystalline Metal Oxides

Efficient Catalytic Decomposition of N2O over Cd-doped NiO in the Presence of O2

Catalytic Decomposition of N2o on Zro2 and Co/Ni/Zro2 Systems

Catalytic Decomposition of Nitrous Oxide on Grafted CuO/γ-Al2O3 Catalysts

DIRECT DECOMPOSITION OF NITRIC OXIDE UPON CATALYST DERIVED FROM CALCINED Co-Al HYDROTALCITE-LIKE COMPOUND

Catalytic Decomposition of N2o over Cu-Zsm-5 Nanosheets

Catalytic decomposition of N<sub>2</sub>O over Rh/Zn–Al<sub>2</sub>O<sub>3</sub> catalysts

Catalytic Decomposition of N<sub><sub>2</sub>O</sub>ON ZrO<sub><sub>2</sub></sub>and Co/Ni/ZrO<sub>2</sub>Systems

Decomposition of Nitrous Oxide over a Low‐cost Catalyst

The Oscillatory Behaviour of Cu‐ZSM‐5 Catalysts for N2O Decomposition: Investigation of Cu species by complementary techniques

Catalytic Decomposition of Nitric Oxide over Nano-sized PbTiO3 loaded Cupric Oxide

Effect of Cesium Modification on CuO/CeO 2 Catalysts for the Catalytic Decomposition of N 2 O

Direct catalytic decomposition of N2O over bismuth modified NiO catalysts

Low-Temperature Decomposition of Nitrous Oxide on Cs/MexCo3-xO4 (Me: Ni or Mg, x = 0–0.9) Oxides

Catalytic Decomposition of N2o over Rhox Supported on Metal Phosphates

Balance Between Reducibility and N2O Adsorption Capacity for the N2O Decomposition: CuxCoy Catalysts As an Example

Bimetallic Au-Pd alloy catalysts for N 2O decomposition: Effects of surface structures on catalytic activity