Abstract:The rare earth (RE) based alloys or compounds with excellent cryogenic magnetocaloric performance have received much research interest recently due to their potential applications of environmental friend magnetic refrigeration (MR) technology. Herein, three ternary RE-based carbide compounds RE2Cr2C3 (RE = Er, Ho, and Dy) were synthesized, an investigation of combined experimental and theoretical has been performed with regard to crystal structure, magnetic properties, magnetic phase transition as well as the magnetocaloric effect (MCE) and magnetocaloric performance. All the RE2Cr2C3 carbide compounds are crystallized in the orthorhombic type crystal structure (C12/m1 space group). The magnetic ground state was confirmed to be ferromagnetic (FM) for Er2Cr2C3, whereas antiferromagnetic (AFM) for Ho2Cr2C3 and Dy2Cr2C3 compounds by density functional theory calculation in addition to experimental observation. Large cryogenic MCE has been observed with the maximum isothermal magnetic entropy change (triangle S-M(max)) of 15.20, 13.98 and 9.04 J/kgK for Er2Cr2C, Ho2Cr2C3 and Dy2Cr2C3 under the magnetic field change (triangle H) of 0-5 T, respectively. Additionally, low field table-like MCE has been achieved in the Er2Cr2C3/Ho2Cr2C3 composites, which is benefit for active applications. These results assess and highlight the potential applicative interest of RE2Cr2C3 carbide compounds in the field of cryogenic MR.

Improvement of critical current density of RE Ba2Cu3O7-δ by increase in configurational entropy of mixing

Improvement of local critical current density of REBa2Cu3O7-d by the increase in configurational entropy of mixing at the RE site

Synthesis of RE123 high-Tc superconductors with a high-entropy-alloy-type RE site

Influences of thermodynamic factors on formation of RE1+xBa2-xCu3Oz superconductivity

Systematic Enhancement of In-Field Critical Current Density with Rare-Earth Ion Size Variance in Superconducting Rare-Earth Barium Cuprate Films

Effects of equivalent composition on superconducting properties of high-entropy REOBiS$_2$ (RE = La, Ce, Pr, Nd, Sm, Gd) single crystals

Excellent Magnetocaloric Performance in the Carbide Compounds RE2Cr2C3 (RE = Er, Ho, and Dy) and Their Composites

Enhancement of Pinning Role by Nonstoichiometry in YBa2Cu3O7−y Superconductors

Manufacture and characterization of RE 2 Co (RE=Gd, Ho) amorphous alloys with excellent magnetic entropy change

Atomic Origin of the Coexistence of High Critical Current Density and High T C in CuBa 2 Ca 3 Cu 4 O 10+δ Superconductors

Nucleation and epitaxy growth of high-entropy REBa2Cu3O7– (RE= Y, Dy, Gd, Sm, Eu) thin films by metal organic deposition

Significant improvement of the critical current of MOD-derived YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ </sub>-coated conductors by post-annealing treatment

Growth of REBa2Cu3Ox single-crystal whiskers utilizing the concept of high-entropy alloys

Significant improvement of the critical current of MOD-derived YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-<i></i></sub> -coated conductors by post-annealing treatment

RE BCO mixtures with large difference in rare-earth ion size: superconducting properties of chemical solution deposition-grown Yb 1− x Sm x Ba 2 Cu 3 O 7− δ films

Improvement of Surface Morphology and Critical Current Density of YDy 0 . 2 Ba2Cu 3 . 3 O7−δ Thick Films by Inserted RE2O3 Thin Films

Effect of Er/Y addition on the growth and superconductivity of Bi2212 films

Performance improvement and element segregation behavior in Y substituted nanocrystalline (La,Ce)–Fe–B permanent magnetic alloys without critical RE elements

Nucleation and Epitaxy Growth of High-Entropy REBa2Cu3O7-δ(RE=Y,Dy,Gd,Sm,Eu)thin Films by Metal Organic Deposition

Key factor for low anisotropy and high irreversibility field in (Cu,C)Ba2Ca3Cu4O11+δ

Key Factor for Enhancing High Power Applications in Cuprate Superconductors