Effect of a High Temperature Brazing Thermal Cycle on the Microstructure and Mechanical Properties of Fe–Cr–Mn–Ni–C Stainless Steel
S. Chenna Krishna,T. Venkateswaran,Gundi Sudarsana Rao,Sushant K. Manwatkar,Pravin Muneshwar,B. Govind,P. Ramesh Narayanan,M. Mohan
DOI: https://doi.org/10.1007/s13632-023-00963-1
2023-04-30
Metallography, Microstructure, and Analysis
Abstract:This study investigates the effect of a brazing thermal cycle on the microstructure and mechanical properties of Fe–Cr–Mn–Ni–C stainless steel using microstructural examination, X-ray diffraction, ferrite content, hardness, impact, and tensile testing. Stainless steel was exposed to a high-temperature brazing thermal cycle of 1180 °C for 20 min, followed by different cooling practices, including furnace, air, and water quenching. The microstructure of the as-received steel mainly comprised austenite, ferrite, sigma phase, and carbides. Air and furnace cooling resulted in the formation of a sigma phase by decomposition of the ferrite phase. The amount of sigma phase varied depending on the cooling rate, which in turn influenced the mechanical properties. Water-quenched specimens were free from the sigma phase, while furnace-cooled specimens had a sigma phase of 9%. In other conditions, the sigma phase was in the range of 2.5–4%. Furnace-cooled specimens with higher sigma phase exhibited lower tensile ductility and impact strength compared to other conditions due to the brittle nature of the sigma phase. Re-solution treatment of furnace-cooled specimens at 1050 °C reduced the sigma phase and restored the mechanical properties.