Abstract:The structural, magnetocaloric, and magnetic characteristics in Heusler Ni50Mn35In10X5 (X = Ga, Fe, and Al) alloys were examined using X-ray diffraction and field-dependent magnetization measurements. All samples exhibited a mixture structure of cubic L21 and tetragonal L10 and underwent second-order magnetic transitions at TC(Al5) = 220 K, TC(Ga5) = 252 K, and TC(Fe5) = 298 K. The Ga5 alloy exhibited structural change as indicated by a thermal hysteresis that may be seen in the saturation magnetic field in the M(T) dependences. The transition at the TC point from a ferromagnetic to a paramagnetic state caused a drop in magnetization, supported by thermal hysteresis, at a low magnetic field (0.01 T). On the other hand, the Fe5 alloy presented a gradual decrease in magnetization with similar hysteresis behavior, also at a low magnetic field (0.01 T), whereas at 0.1 T of field, no features characteristic of this transition were detected. This could be due to a large difference in the metallic radius of Fe compared to that of In. Otherwise, magnetic investigations demonstrated that the replacement of In with Al may cause the structural transformation temperatures and TC to be shifted to low temperatures. The present results imply that the structural transformation temperatures and the transition itself are highly dependent on chemical composition. Furthermore, under a magnetic field change of 5 T, the maximum magnetic entropy changes of 0.6 J/kg K, 1.4 J/kg K, and 2.71 J/kg K for the Ga5, Fe5, and Al5 alloys, respectively, were determined by their TC. Refrigeration capacity values were found to be 25 J/kg, 74 J/kg, and 98 J/kg at µ0∆H = 5 T. These ribbons are viable candidates for multifunctional applications due to their cheaper cost and their physical characteristics disclosed during the magnetostructural transition, which takes place close to the room temperature.

The Effects of Magnetic and Non-magnetic Element Substitutions in Ni-Mn-Ga Alloy

Tunable Magnetocaloric Effect in Ni-Mn-Ga Microwires.

Large Field-Induced Magnetocaloric Effect in Ni$_{43}$Mn$_{46 - {\rm X}}$v$_{\rm X}$sn$_{11}$ Heusler Alloys

Experimental investigation of martensitic transformation in Ni2MnGa alloys with elemental substitutions

New biology of red rain extremophiles prove cometary panspermia

Reversible Magnetic-Field-induced Martensitic Transformation over a Wide Temperature Window in Ni42−xCoxCu8Mn37Ga13 Alloys

Influence of Al Substitution on the Magnetocaloric and Magnetoresistance Effects of Ni46Co4Mn38Sb12−Al (0 ≤ X ≤ 2) Alloys

The magnetostructural transformation and magnetocaloric effect in Co-doped MnNiGe<sub>1.05</sub>alloys

Phase Transition of Ni 55− X Co X Mn 20 Ga 25 (8.5 ≤ X ≤ 11.0) Alloys with Different Compositions and Magnetic Fields

Influence of intermartensitic transitions on transport properties of Ni2.16Mn0.84Ga alloy

Controlling magnetostructural transition and magnetocaloric effect in multi-component transition-metal-based materials

Phase transition of Ni55-xC0xMn20Ga25(8.5≤x≤11.0)alloys with different compositions and magnetic fields

Effects of Co and Si co-doping on magnetostructural transformation and magnetocaloric effect in Ni-Mn-Sn based alloys

Effect Of Isoelectronic Substitution On Phase Transition And Magnetic Properties Of Ni57mn18ga25-Xinx(0 <= X <= 8) Alloys With Ni Excess

Magnetoresistance and Magnetocaloric Effect in Metamagnetic Alloys Ni45co5mn36.5in13.5

Room Temperature Magnetocaloric Effect in Ni-Mn-In

Magnetic-Field-Induced Martensitic Transformation in Mnniga : Co Alloys

The Effects of La Doping on the Crystal Structure and Magnetic Properties of Ni2In-Type MnCoGe1−xLax (x = 0, 0.01, 0.03) Alloys

Giant Magnetocaloric and Magnetoresistance Effects in Ferrimagnetic Mn1.9co0.1sb Alloy

Effect of Co Addition on the Martensitic Transformation and Magnetocaloric Effect of Ni–Mn–Al Ferromagnetic Shape Memory Alloys

Structural, Magnetocaloric, and Magnetic Properties in Heusler Ni50Mn35In10X5 (X = Ga, Fe and Al) Alloys