Abstract:The impact of a titania (TiO2) support film surface on the catalytic activity of gold nanoparticles (Au NP) was investigated. Using the reactive dc-magnetron sputtering technique, TiO2 films with an amorphous, anatase, and nitrogen-doped anatase crystal structure were produced for a subsequent role as a support material for Au NP. Raman spectra of these TiO2 films revealed that both vacuum and NH3 annealing treatments promoted amorphous to anatase phase transformation through the presence of a peak in the 513-519 cm-1 spectral regime. Furthermore, annealing under NH3 flux had an associated blue shift and broadening of the Raman active mode at 1430 cm-1, characteristic of an increase in the oxygen vacancies (VO). For a 3 to 15 s sputter deposition time, the Au NP over TiO2 support films were in the 6.7-17.1 nm size range. From X-ray photoelectron spectroscope (XPS) analysis, the absence of any shift in the Au 4f core level peak implied that there was no change in the electronic properties of Au NP. On the other hand, spontaneous hydroxyl (-OH) group adsorption to anatase TiO2 support was instantly detected, the magnitude of which was found to be enhanced upon increasing the Au NP loading. Nitrogen-doped anatase TiO2 supporting Au NP with ~21.8 nm exhibited a greater extent of molecular oxygen adsorption. The adsorption of both -OH and O2 species is believed to take place at the perimeter sites of the Au NP interfacing with the TiO2 film. XPS analyses and discussions about the tentative roles of O2 and -OH adsorbent species toward Au/TiO2 systems corroborate very well with interpretations of density functional theory simulations.

Au 9 Nanocluster Adsorption and Agglomeration Control through Sulfur Modification of Mesoporous TiO 2

Au 9 clusters deposited as co-catalysts on S-modified mesoporous TiO 2 for photocatalytic degradation of methyl orange

Synthesis and structure characterization of nanosized Au clusters on titania-modified mesoporous MCM-41

Au9 clusters deposited as co-catalysts on S-modified mesoporous TiO2 for photocatalytic degradation of methyl orange

Atomic layer deposition of TiO2 on mesoporous silica

Modification of Titanium Dioxide Nanoparticles with 3-(Trimethoxysilyl)propyl Methacrylate Silane Coupling Agent

Preparation of Mesoporous Ag-containing TiO2 Heterojunction Film and Its Photocatalytic Property

Reduced Sintering of Mass-Selected Au Clusters on SiO2by Alloying with Ti: an Aberration-Corrected STEM and Computational Study

TiO2 mesoporous thin film architecture as a tool to control Au nanoparticles growth and sensing capabilities

Synthesis and Characterization of Pt, Au or Pd Clusters Deposited Titania-Modified Mesoporous Silicate MCM-41

Surface Modification of Au/Tio2 Catalysts by Sio2 Via Atomic Layer Deposition

Controllably partial removal of thiolate ligands from unsupported Au 25 nanoclusters by rapid thermal treatments for electrochemical CO 2 reduction

Enhanced Photocatalytic Degradation of Methyl Orange Using Nitrogen‐Functionalized MesoporousTiO2 Decorated with Au9 Nanoclusters

High-Surface-Area Mesoporous Crystalline TiO2: Synthesis, Characterization, and Application As Support for Making Stable Au Catalysts

X-ray Photoelectron Spectroscopy (XPS) Analysis of Ultrafine Au Nanoparticles Supported over Reactively Sputtered TiO2 Films

Size and Shape Dependence of the Electronic Structure of Gold Nanoclusters on TiO2.

Synthesis of Fully Exposed Single‐Atom‐Layer Metal Clusters on 2D Ordered Mesoporous TiO2 Nanosheets

Silylation Modification on Surface of Ti-MCM-41 Molecular Sieves

Sulfur nanoparticles in situ growth on TiO2 mesoporous single crystals with enhanced solar light photocatalytic performance

Sono- and Photochemical Routes for the Formation of Highly Dispersed Gold Nanoclusters in Mesoporous Titania Films

Manipulating the charge state of Au clusters on rutile TiO2(110) single crystal surfaces through molecular reactions probed by infrared spectroscopy