Abstract:Ethylenediamine-doped (EDA-doped) polyaniline (PANI) films were deposited via spin coating technique on a glass substrate. The samples were annealed at different times and temperatures. The characterizations of the prepared PANI films were described by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy (FT-IR). It is found that the conductivity changes under deep mouth exhaling for 150/1 h sample is 1.65 times faster than the films annealed at 100°C/4 h. The response and recovery time of the 150/1 h EDA-doped PANI film is decreased by order of 0.63 and 1.29 s than those films dried at 100°C for 4 h, respectively. The 150/1 h EDA doped PANI film during deep exhaling its conductivity increased abruptly from 2.2 × 10 –7 to 0.026 S/cm –1 . In a few seconds, following an inhalation, there occurs a complete transition to the dry state conductivity. Furthermore, the increment in conductivity of the EDA-doped PANI films was determined at various RH levels (20, 40, 60, 80, and 90%) with exposure and evacuation of the humid air. The doped PANI sample annealed at 150°C for 1 h exhibit the highest conductivity at 90% RH. The conductivity was increased from 2.16 × 10 –7 S/cm for the insulating state at the dry state to 0.23 S/cm for the semiconducting state at 90% RH. Consequently, the 150/1 h sample showed an increase in conductivity by order of 10 6 at 90% RH. For all samples, the conductivity progressively rises as the RH value increases till 90% of RH value samples exhibit an abrupt increase in conductivity except the 100°C/4 h sample. The highest conductivity is 0.041 S/cm at 90% RH obtained for the case of 150/30 min sample, whereas the 150/1 min and 100/4 h films show maximum conductivity of 0.027 and 0.007, respectively.

Investigating ion irradiation effects for modifying optical properties of CA/PANI films

Impacts of Low Energy Argon Beam on Enhancing the Surface Wettability and Electrical Performance of CA/PANI Films

Enhancing the dielectric characteristics of argon beam irradiated polymer composite films

Influence of ion beam and silver nanoparticles on dielectric properties of flexible PVA/PANI polymer composite films

Influence of argon irradiations on modifying the surface properties and optical behavior of polymer composite films

Synthesis, Structural Investigations, and Dielectric Properties of Irradiated Flexible Polymeric Composite Films

Augmentation of room temperature gas sensing properties of PANI thin films by 100 keV Ar + ion irradiation

Study Effect Alpha Irradiation with Annealing on Chemical - Optical Properties of Poly (methyl methacrylate) Films

Characterization and linear / nonlinear optical aspects of polyaniline (PANI) films incorporated with Ethylenediamine for low-cost limiting optical technologies

Influence of ion beam on the surface characteristics and structural properties of PVA/TiO 2 films

Structural and optical studies of gamma-irradiated polyvinyl alcohol, polyethylene glycol, and lignosulfonate thin film

Effect of gamma irradiation on properties of the synthesized PANI-Cu nanoparticles assimilated into PS polymer for electromagnetic interference shielding application

Influence of Ion Irradiation on the Surface Properties of Silver-Coated Flexible PDMS Polymeric Films

Electrical and Optical Properties of PANI-C60 Composite Films

A comparative study of gamma radiation-induced modifications in optical and structural properties of PANI/PVC composites

Impacts of Low Energy Oxygen Irradiation on the Dielectric Properties of PVA/TiO2 Nanocomposite Films

Iron-Oxide-Nanoparticles-Doped Polyaniline Composite Thin Films

Irradiation Effect in Thermoelectric Polymer Polyaniline Induced by High-Energy Electron Beam

Tailoring physical properties and electrochemical performance of polyaniline thin films via chemical bath deposition

Achieving variable infrared emissivity modulation regions of poly(aniline) films:the effect of film surface morphology on the optical tunability

Investigation of Insulator-to-Semiconductor Fast Transition in Sheet-Like Polyaniline Films