Abstract:Soy protein isolate (SPI) is an attractive natural material for preparing wood adhesives that has found broad application. However, poor mechanical properties and unfavorable water resistance of wood composites with SPI adhesive bonds limit its more extensive utilization. The combination of lysine (Lys) with a small molecular structure as a curing agent for modified soy-based wood adhesive allows Lys to penetrate wood pores easily and can result in better mechanical strength of soy protein-based composites, leading to the formation of strong chemical bonds between the amino acid and wood interface. Scanning electron microscopy (SEM) results showed that the degree of penetration of the S/G/L-9% adhesive into the wood was significantly increased, the voids, such as ducts of wood at the bonding interface, were filled, and the interfacial bonding ability of the plywood was enhanced. Compared with the pure SPI adhesive, the corresponding wood breakage rate was boosted to 84%. The wet shear strength of the modified SPI adhesive was 0.64 MPa. When Lys and glycerol epoxy resin (GER) were added, the wet shear strength of plywood prepared by the S/G/L-9% adhesive reached 1.22 MPa, which increased by 29.8% compared with only GER (0.94 MPa). Furthermore, the resultant SPI adhesive displayed excellent thermostability. Water resistance of S/G/L-9% adhesive was further enhanced with respect to pure SPI and S/GER adhesives through curing with 9% Lys. In addition, this work provides a new and feasible strategy for the development and application of manufacturing low-cost, and renewable biobased adhesives with excellent mechanical properties, a promising alternative to traditional formaldehyde-free adhesives in the wood industry.

Synergistic effect of lignin and ethylene glycol crosslinked epoxy resin on enhancing thermal, mechanical and shape memory performance

Effect of graphene nanosheets and layered double hydroxides on the flame retardancy and thermal degradation of epoxy resin

Simultaneously reinforcing and toughening of shape-memory epoxy resin with carboxylated lignosulfonate: Facile preparation and effect mechanism

Molecular Dynamics Simulations of Mechanical Properties of Epoxy-Amine: Cross-linker Type and Degree of Conversion Effects

Preparation of carboxylated lignin-based epoxy resin with excellent mechanical properties

Enhancing mechanical properties of epoxy resin using waste lignin and salicylate alumoxane nanoparticles

Synthesis of a novel lignin‐based epoxy resin curing agent and study of cure kinetics, thermal, and mechanical properties

Effect of lignin on the structure-property behavior of metal-coordinated and chemically crosslinked ethylene-propylene-diene-monomer composites

Lignin-based silicone-modified epoxy resin with enhanced strength and toughness

Effect of curing agents n‐octylamine and m‐xylene diamine on the mechanical and memory properties of E51 epoxy resin

Performance of UV Curable Lignin Based Epoxy Acrylate Coatings

Facile Synthesis of Intrinsically Flame‐retardant Epoxy Thermosets with High Mechanical Properties from Lignin Derivatives

Study on the preparation of epoxy resin materials from nano-lignin polyols

Epoxy-functionalized polysiloxane/Nano-SiO2 synergistic reinforcement in cryogenic mechanical properties of epoxy and carbon fiber reinforced epoxy laminate

Synthesis of an alkynyl‐ and allyla‐ terminated modifiers and its thermal and mechanical properties in copolymer with epoxy resin

Effects of Chemical Composition and Cross-Linking Degree on the Thermo-Mechanical Properties of Bio-Based Thermosetting Resins: A Molecular Dynamics Simulation Study

Impact Of Lignin Source On The Performance Of Thermoset Resins

Engineering phosphorus-containing lignin for epoxy biocomposites with enhanced thermal stability, fire retardancy and mechanical properties

Synchronously Improving Mechanical and Thermal Performances of Cured Epoxy Resins by Epoxidized Polyether Sulphones As Modifiers

A lignin-based epoxy/TiO2 hybrid nanoparticle for multifunctional bio-based epoxy with improved mechanical, UV absorption and antibacterial properties

Effects of Lysine on the Interfacial Bonding of Epoxy Resin Cross-Linked Soy-Based Wood Adhesive