Abstract:The hydration process and compressive strength and flexural strength development of sulphate-resistant Portland cement (SRPC) curing at 20 °C, 40 °C, 50 °C, and 60 °C were studied. In addition, MIP, XRD, SEM, and a thermodynamic simulation (using Gibbs Energy Minimization Software (GEMS)) were used to study the pore structure, the types, contents, and transformations of hydration products, and the changes in the internal micro-morphology. The results indicate that, compared with normal-temperature curing (20 °C), the early compressive strength (1, 3, and 7 d) of SRPC cured at 40~60 °C increased by 10.1~57.4%, and the flexural strength increased by 1.8~21.3%. However, high-temperature curing was unfavorable for the development of compressive strength and flexural strength in the later period (28~90 d), as they were reduced by 1.5~14.6% and 1.1~25.5%, respectively. With the increase in the curing temperature and curing age, the internal pores of the SRPC changed from small pores to large pores, and the number of harmful pores (>50 nm) increased significantly. In addition, the pore structure was further coarsened after curing at 60 °C for 90 d, and the number of multiple harmful pores (>200 nm) increased by 17.9%. High-temperature curing had no effect on the types of hydration products of the SRPC but accelerated the formation rate of hydration products. The production of the hydration products C-S-H increased by 13.5%, 18.6%, and 22.8% after curing at 40, 50, and 60 °C for 3 d, respectively. The stability of ettringite (AFt) reduced under high-temperature curing, and its diffraction peak was not observed in the XRD patterns. When the curing temperature was higher than 50 °C, AFt began to transform into monosulfate, which consumed more tricalcium aluminate hydrate and inhibited the formation of “delayed ettringite”. Under high-temperature curing, the compactness of the internal microstructure of the SRPC decreased, and the distribution of hydration products was not uniform, which affected the growth in its strength during the later period.

Time-dependent rheological analysis of self-consolidating concrete mixtures considering various mixing temperatures

Investigating the Effects of Mixing Time and Mixing Speed on Rheological Properties, Workability, and Mechanical Properties of Self-Consolidating Concretes

Study on Shear Behavior of Concrete-polymer Cement Mortar at Elevated Temperature

Influence of Mixture Proportions on Fresh and Mechanical Properties of Self-consolidating Concrete

Investigation on Concrete-Pcm Interface under Elevated Temperature: at Material Level and Member Level

Fresh, Durability and Mechanical Behavior of Self Consolidating Concrete Incorporating Fly Ash and Admixture under Hot Weather

Performance of steel fibers reinforced self compacting concrete subjected to high temperature

Influence of mixing time and superplasticizer dosage on self-consolidating concrete properties

Effect of Variations in Aggregate Ratios on the Fresh, Hardened, and Durability Properties of Self-Compacting Concrete

Impact of Hot Weather Conditions on the Performance of Supplementary Cementitious Materials Concrete

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers

Microstructural study of concrete performance after exposure to elevated temperatures via considering C–S–H nanostructure changes

Performance of Different Concrete Types Exposed to Elevated Temperatures: A Review

Residual Compressive Behavior of Self-Compacting Concrete after High Temperature Exposure—Influence of Binder Materials

Study on the Strength and Hydration Behavior of Sulfate-Resistant Cement in High Geothermal Environment

THE EFFECTS OF HIGH TEMPERATURE CURING ON HYDRATION REACTION AND STRENGTH DEVELOPMENT OF CEMENT PASTE CONTAINING SILICA FUME AT LOW WATER BINDER RATIO

Experimental Study of Thermal-Hydraulic-Mechanical Coupling Behavior of High-Performance Concrete

Comparative analysis of dynamic mechanical properties of steel fiber reinforced concrete under ambient temperature and after exposure to high temperatures

Effect of high temperature on the mechanical properties of basalt fibre self-compacting concrete as an overlay material

Effect of Temperature on Pore Structure and Strength of Concrete

Influence of Elevated Temperatures on the Compressive Strength of Concrete Made with Different Types of Aggregate