Abstract:In this work, we reported that the fibrous silica nanosphere, also called as KCC-1, was facilely synthesized by the improved microemulsion hydrothermal fabrication strategy. The obtained KCC-1 was investigated as the support of the Ni based catalysts toward CO2 methanation. The obtained catalysts with unique dendrimeric mesopore structure and outstanding structural properties could provide easily accessible as well as highly dispersed Ni nanoparticles to the gaseous reactants. Besides, the Ni based catalysts with commercial SiO2 and MCM-41 as supports were also prepared as the reference catalysts to demonstrate the advantages of the dendrimeric mesoporous channels. Various techniques, such as X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), H-2 temperature programmed reduction (H-2-TPR), CO2 temperature programmed desorption (CO2-TPD), X-ray photoelectron spectroscopy (XPS), etc., were used to characterize the catalytic supports and corresponding catalysts. It was found that the metallic Ni nanoparticles could be highly dispersed over the catalysts supported on fibrous KCC-1 with dendrimeric mesoporous channels. Furthermore, the catalytic performances toward CO2 methanation had been further evaluated over these catalysts at different temperatures. It was found that the KCC-1 supported catalyst performed much higher low-temperature catalytic activities than the reference catalysts supported on commercial SiO2 and MCM-41, suggesting that the fibrous and dendrimeric mesoporous channels displayed distinctive advantages by accommodating enough metallic Ni active sites. The kinetic study also revealed that the topology of the mesoporous channel could obviously influence the apparent activation energy in the CO2 methanation reaction. Besides, the temperature programmed surface reaction (TPSR) and in-situ Diffused Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) of the CO2 methanation were also carried out to reveal the possible reaction pathway and mechanism. We also found that the fibrous silica nanosphere (KCC-1) supported catalyst demonstrated much better sintering-proof property of the metallic Ni nanoparticles than the reference catalysts during the 40 h stability tests at 400 degrees C. Therefore, the present fibrous silica nanosphere (KCC-1) could be considered as the promising support for Ni based catalysts toward CO2 methanation.

Size-controllable carbon spheres doped Ni (II) for enhancing the catalytic oxidation of methanol

S,N dual-doped carbon nanotubes as substrate to enhance the methanol oxidation performance of NiO nanoparticles

Facilely Fabricating Highly Dispersed Ni-based Catalysts Supported on Mesoporous MFI Nanosponge for CO2 Methanation

Atomic-Dispersed Coordinated Unsaturated Nickel–Nitrogen Sites in Hollow Carbon Spheres for the Efficient Electrochemical CO 2 Reduction

Sodium Dodecyl Sulfate-Assisted Hydrothermal Synthesis of Mesoporous Nickel Cobaltite Nanoparticles with Enhanced Catalytic Activity for Methanol Electrooxidation

In situ growth of Ni/Ni3S2–MoO2 nanocrystals on carbon cloth for the enhanced electrocatalytic oxidation of methanol

Efficient synergism of concentric ring structures and carbon dots for enhanced methanol electro-oxidation

Facile preparation of a Ni/MgAl2O4 catalyst with high surface area: enhancement in activity and stability for CO methanation

Hierarchical PdNi alloy nanochains coupled with Ni(OH)2 nanosheets to enhance CO-poisoning resistance for the methanol oxidation reaction

Tailoring the electronic structure of PtNi nanoalloy for boosting methanol electro-oxidation reaction

Modulating Electronic Structure of Ni/carbon Spherical Nano-superstructures through Transition Metal-doping as Highly Efficient Catalysts for Hydrogen Evolution Reaction

Carbon dots-induced carbon-coated Ni and Mo2N nanosheets for efficient hydrogen production

Atomically Dispersed Ni-Based Anti-Coking Catalysts for Methanol Dehydrogenation in a Fixed-Bed Reactor

Construction of Ni/In2O3 Integrated Nanocatalysts Based on MIL-68(In) Precursors for Efficient CO2 Hydrogenation to Methanol

Environmentally friendly PtNiCo nanocatalysts enhanced with multi-walled carbon nanotubes for sustainable methanol oxidation in an alkaline medium

Ni3C/Ni3S2 Heterojunction Electrocatalyst for Efficient Methanol Oxidation via Dual Anion Co-modulation Strategy

Pt-Ni Alloyed Nanocrystals With Controlled Architectures For Enhanced Methanol Oxidation

Constructing Highly Dispersed Ni Based Catalysts Supported on Fibrous Silica Nanosphere for Low-Temperature CO2 Methanation

Mof Derived Carbon Encapsulation Coni Nanocrystal In-Situ Grafting of N-Doped Carbon Nanotubes for Synergistically Enhancing Electrocatalytic Active for Methanol Oxidation

Ultrasonic-assisted Synthesis of Pd–Ni Alloy Catalysts Supported on Multi-Walled Carbon Nanotubes for Formic Acid Electrooxidation

New strategy of S,N co-doping of conductive-copolymer-derived carbon nanotubes to effectively improve the dispersion of PtCu nanocrystals for boosting the electrocatalytic oxidation of methanol