Beneficial Utilization of Rice Husk Ash (rha) As A New Sorbent for Removal of Antimony (iii) from Water
Kejia Zhang,Tuqiao Zhang,Yang Deng,Lei Li,Yiping Zhang
2013-01-01
Fresenius environmental bulletin
Abstract:This study represents the first scientific effort to evaluate the technical feasibility of rice husk ashes (RHA; ash burned after RH) as a new water treatment material for adsorption of Sb(III) from drinking water. Three RHA samples (RHA300, RHA450, RHA600) were prepared from RH at 300, 450 and 600 degrees C, respectively. Compared with RH, RHA had great specific surface areas, small particle sizes, and large total pore volumes. Moreover, the RHA was characterized by an amorphous structure. In the subsequent bench-scale tests, the RHA samples were utilized to adsorb Sb(III) from water. Kinetics tests showed that pseudo first-order and pseudo second-order kinetics models both well fit the experimental data, and Sb(III) sorption rates followed the order of RHA450 > RHA600 > RHA300 > RH. Among the 4 tested adsorption isotherm models (Freundlich, Langmuir, Temkin, and Dubinin-Radushkevich), the Langmuir isotherm was the best one to fit the measured data, and the adsorption capacities of RHA300, RHA450 and RHA600 were 1.407, 3.842 and 2.731 mg/g, respectively. Solution pH, natural organic matters (NOMs) and certain cations (e.g. Fe3+ and Fe2+) were significant factors controlling the adsorption process. RHA300 adsorption was increased with increasing pH from 2 to 12, while RHA450 and RHA600 showed a high adsorption potential at pHs 4-10. Their maximum adsorption capacities were observed at pH values where the lowest zeta potentials were found. Fe3+ and Fe2+ both greatly inhibited RHA adsorption of Sb(III). In contrast, K+, Na+, Mn2+ and Cu2+, as well as humic acid (HA) (the major NOM fraction), had a minor impact upon the adsorption. Our results demonstrate that RHA is a technically effective sorbent to address the Sb(III) pollution in water.