Abstract:The aim of this study is to analyze the ballistic impact behavior of a panel made of Twaron CT736 fabric with a 9 mm Full Metal Jacket (FMJ) projectile. Three shots are fired at different velocities at this panel. The ballistic impact test procedure was carried out in accordance with NIJ 010106. The NIJ-010106 standard is a document that specifies the minimum performance requirements that protection systems must meet to ensure performance. The 9 mm FMJ projectile is, according to NIJ 010106, in threat level II, but the impact velocity is in threat level IIIA. Analysis of macro-photographs of the impact of the Twaron CT736 laminated fabric panel with a 9 mm FMJ projectile involves a detailed examination of the images to gather information about the material performance and failure mechanisms at the macro- or even meso-level (fabric/layer, thread). In this paper, we analyze numerically and experimentally a panel consisting of 32 layers, made of a single material, on impact with a 9 mm FMJ projectile. The experimental results show that following impact of the panel with three projectiles, with velocities between 414 m/s and 428 m/s, partial penetration occurs, with a different number of layers destroyed, i.e., 15 layers in the case of the projectile velocity of 414 m/s, 20 layers of material in the case of the panel velocity of 422 m/s and 22 layers destroyed in the case of the projectile velocity of 428 m/s. Validation of the simulated model is achieved by two important criteria: the number of broken layers and the qualitative appearance. Four numerical models were simulated, of which three models validated the impact results of the three projectiles that impacted the panel. Partial penetration occurs in all four models, breaking the panel in the impact area, with only one exception, i.e., the number of layers destroyed, in which case the simulation did not validate the validation criterion. The performance of Twaron CT736 fabric is also given by the indentation depth values by two methods: according to NIJ 0101.06 and by 3D scanning. The NIJ 010106 standard specifies that a panel provides protection when the indentation depth values are less than 0.44 mm.

Postmortem Analysis Using Different Sensors and Technologies on Aramid Composites Samples after Ballistic Impact

A Computational Analysis of the High-velocity Impact Performance of Lightweight 3D Hybrid Composite Armors

Dynamic Impact Surface Damage Analysis of 3D Woven Para-Aramid Armour Panels Using NDI Technique

Dynamic Response and Research of 3D Braided Carbon Fiber Reinforced Plastics Subjected to Ballistic Impact Loading

Assessment of Multilayered Plates with Hyperelastic Coatings Subjected to Dynamic Loadings by Impact at Low Velocities

A combined experimental/numerical study on the scaling of impact strength and toughness in composite laminates for ballistic applications

Experimental and Numerical Analysis of the Damage Mechanism of an Aramid Fabric Panel Engaged in a Medium-Velocity Impact

The Behaviour of Stratified Fabrics of Aramid Fibres under Stabbing Conditions

Full-field Transient 3D Deformation Measurement of 3D Braided Composite Panels During Ballistic Impact Using Single-Camera High-Speed Stereo-Digital Image Correlation

Fractographic Analysis of High Performance Fabric Reinforced Composites after Ballistic Impact

Study of Dynamic Impact Behaviors and Ballistic Properties of Hybrid Composites

Shattering Effect Study of Aramid–Steel Composite Target Plates under Localized Blast Loading

Numerical simulation of ballistic impact on composite armours

Micromechanics-based multi-scale framework with strain-rate effects for the simulation of ballistic impact on composite laminates

Numerical modeling and analysis of the ballistic impact response of ceramic/composite targets and the influence of cohesive material parameters

Design and Ballistic Performance of Hybrid Plates Manufactured from Aramid Composites for Developing Multilayered Armor Systems

Ballistic Resistance of 2D and 3D Woven Sandwich Composites

Automated Impact Damage Detection Technique for Composites Based on Thermographic Image Processing and Machine Learning Classification

Experimental Investigations Regarding the Behaviour of Composite Panels Based on Polyurea and Kevlar or Dyneema Layers Under Blast and Fragments

Experimental investigation on high-velocity impact damage and compression after impact behavior of 2D and 3D textile composites

Low-velocity impact and quasi-static post-impact compression analysis of woven structural composites for automotive: Influence of fibre types and architectural structures