Electrochemical polymerization of anilinium hydrochloride

Yomen Atassi,Mohammad Tally

DOI: https://doi.org/10.48550/arXiv.1307.5668

2013-07-22

Materials Science

Abstract:Electropolymerization of anilinium hydrochloride was carried out on platinum plate electrode in a protic medium by cyclic voltammetry. The effects on the electrodeposition of the sweep rate, monomer concentration, pH of the medium and electrode nature are discussed.

What problem does this paper attempt to address?

Poly(olefin)-Based Anion Exchange Membranes Prepared Using Ziegler–Natta Polymerization

Liang Zhu,Xuedi Yu,Xiong Peng,Tawanda J. Zimudzi,Nayan Saikia,Michael T. Kwasny,Shaofei Song,Douglas I. Kushner,Zhisheng Fu,Gregory N. Tew,William E. Mustain,Michael A. Yandrasits,Michael A. Hickner

DOI: https://doi.org/10.1021/acs.macromol.8b02756

IF: 5.5

2019-01-01

Macromolecules

Abstract:Bromoalkyl-functionalized poly(olefin)s were synthesized by copolymerization of 4-(4-methylphenyl)-1-butene with 11-bromo-1-undecene using Ziegler-Natta polymerization. The resulting bromoalkyl-functionalized poly(olefin)s were converted to quaternary ammonium-containing anion-conductive copolymers by reacting the pendant bromoalkyl group with trimethylamine or a custom-synthesized tertiary amine containing pendant quaternary ammonium moieties. Poly(olefin)-based AEMs with three cations per side chain showed considerably higher hydroxide conductivities, up to 201 mS/cm at 80 degrees C in liquid water, compared to that of samples with only one cation per bromoalkyl site (68 mS/cm, 80 degrees C, liquid water), likely due to phase separation in the triple-cation structure. More importantly, triple-cation side-chain poly(olefin) AEMs exhibited higher hydroxide conductivity under relative humidity conditions (50%-100%) than typical AEMs based on benzyltrimethylammonium cations. The triple-cation the triple-cation side-chain poly(olefin)-based AEM exhibited an ionic conductivity as high as 115 mS/cm under 95% RH at 80 degrees C and 11 mS/cm under 50% RH at 80 degrees C. In addition to high ionic conductivity, the triple-cation side-chain poly(olefin) AEMs exhibited good chemical and dimensional stability. High retention of ionic conductivity (>85%) was observed for the samples in 1 M NaOH at 80 degrees C over 1000 h. Based on these high-performance poly(olefin) AEMs, a fuel cell with a peak power density of 0.94 W cm(-2) (1.28 W cm(-2) after iR correction) was achieved under H-2/O-2 at 70 degrees C. The results of this study suggest a new, low-cost, and scalable route for preparation of poly(olefin)-based AEMs for anion exchange membrane applications.
Role of the Anilinium Ion on the Selective Polymerization of Anilinium 2-Acrylamide-2-methyl-1-propanesulfonate

Alain Salvador Conejo-Dávila,Marco Armando Moya-Quevedo,David Chávez-Flores,Alejandro Vega-Rios,Erasto Armando Zaragoza-Contreras

DOI: https://doi.org/10.3390/polym13142349

2021-07-17

Abstract:The development of anilinium 2-acrylamide-2-methyl-1-propanesulfonate (Ani-AMPS) monomer, confirmed by 1H NMR, 13C NMR, and FTIR, is systematically studied. Ani-AMPS contains two polymerizable functional groups, so it was submitted to selective polymerization either by free-radical or oxidative polymerization. Therefore, poly(anilinium 2-acrylamide-2-methyl-1-propanesulfonic) [Poly(Ani-AMPS)] and polyaniline doped with 2-acrylamide-2-methyl-1-propanesulfonic acid [PAni-AMPS] can be obtained. First, the acrylamide polymer, poly(Ani-AMPS), favored the π-stacking of the anilinium group produced by the inter- and intra-molecular interactions and was studied utilizing 1H NMR, 13C NMR, FTIR, and UV-Vis-NIR. Furthermore, poly(Ani-AMPS) fluorescence shows quenching in the presence of Fe2+ and Fe3+ in the emission spectrum at 347 nm. In contrast, the typical behavior of polyaniline is observed in the cyclic voltammetry analysis for PAni-AMPS. The optical properties also show a significant change at pH 4.4. The PAni-AMPS structure was corroborated through FTIR, while the thermal properties and morphology were analyzed utilizing TGA, DSC (except PAni-AMPS), and FESEM.
Electrosynthesis of poly(aniline-co-p-aminophenol) having electrochemical properties in a wide pH range

Chuanxiang Chen,Cheng Sun,Yuhua Gao

DOI: https://doi.org/10.1016/j.electacta.2007.11.039

IF: 6.6

2008-01-01

Electrochimica Acta

Abstract:Copolymerization of aniline and p-aminophenol in aqueous sulfuric acid solutions was electrochemically performed using cyclic voltammetry on platinum electrodes. The monomer concentration ratio can strongly affect the copolymerization rate and electrochemical property of the copolymer. The optimum conditions for the copolymerization are that the potential sweep covers the −0.20 to 0.95V (vs. SCE) potential range, and that a solution contains 0.18M aniline, 0.02M p-aminophenol and 0.50M H2SO4. A resulting copolymer synthesized under the optimum conditions has a good electrochemical activity in 0.50M solutions of Na2SO4 with pH≤10.0. IR and XPS spectra indicate that –OH groups and SO42− ions are contained in the resulting copolymer. The SEM images reveal that the microstructure of the copolymer depends on the monomer concentration ratio during the electrolysis.
Electrochemical Study of a Polypyrrole Film/Decanethiol Self-Assembled Monolayer on a Gold Electrode

J Wang,BZ Zeng,C Fang,F He,XY Zhou

DOI: https://doi.org/10.1002/(sici)1521-4109(199912)11:18<1345::aid-elan1345>3.0.co;2-t

IF: 3.077

1999-01-01

Electroanalysis

Abstract:Cyclic voltammetry and chronoamperometry were used to study the deposition of polypyrrole on a decanethiol self-assembled monolayer modified gold electrode (PPY/SAM/Au). The voltammetric behavior of the PPY/SAM film was investigated in the presence of several different electrolytes. It is found that the SAM shows great influence on the nucleation and growth of the PPY film. The reaction of the SAM and the anions causes the different voltammetric behavior of the polymerization of pyrrole on the modified electrode. Chronoamperometry shows the nucleation and growth of the PPY is initially inhibited but followed by a rapid increase. The SAM also influences electrochemical behavior of PPY film. Experiments show that the SAM can greatly depress the diffusion of anions in the PPY film, and minimize the background capacitance current.
Chemical Polymerization Method to Synthesize Polyaniline as a Novel Anode Catalyst in Microbial Fuel Cell

R. K. Fakher Al-Fahed,Alaa A. Rashad,Munaf S. Majeed,Hussain A. Badran

DOI: https://doi.org/10.1134/S1560090421060026

2022-02-04

Polymer Science Series B

Abstract:In this work, the chemical polymerization has been employed to synthesis the polyaniline with different concentrations of sulfuric acid. The casting process has been an appropriate method to prepare thin films on the FTO glass. FTIR spectroscopy was used to characteristic IR spectrum vibrational bands of synthesized polymer. The films have been successfully tested as anode in microbial fuel cell application and gave a noticeable effect on the performance of microbial fuel cell system.
Synthesis and Electrochemical Properties of Electroactive Hyperbranched Poly(Aryl Ether Ketone) Bearing Oligoaniline Segments

Fangfei Li,Mingjuan Zhou,Jiayu Wang,Xincai Liu,Ce Wang,Danming Chao

DOI: https://doi.org/10.1016/j.synthmet.2015.03.019

IF: 4

2015-01-01

Synthetic Metals

Abstract:A novel electroactive hyperbranched poly(aryl ether ketone) (EHPAEK) with oligoaniline segments has been prepared by K2CO3-mediated nucleophilic aromatic polycondensation. The structure of EHPAEK was confirmed by Fourier-transform infrared spectra (FTIR), nuclear magnetic resonance (NMR) and gel permeation chromatography (GPC). Its thermal stability and spectroscopic properties were also studied using thermogravimetric analysis (TGA) and UV-vis spectroscopy. Due to the oligoaniline segment, EHPAEK was found to be electroactive, which was explored by cyclic voltammetry in 0.5 M H2SO4. The electrochromism of EHPAEK thin film was examined using EHPAEK/ITO as the working electrode coupled with UV-vis spectroscopy, which exhibited good electrochromic properties with high contrast value, moderate switching times, acceptable coloration efficiency. Furthermore, the Tafel plots analysis and electrochemical impedance spectroscopy was applied to study the anticorrosion of the EHPAEK coatings on the cold rolled steel (CRS) in 3.5 wt% NaCl electrolyte solution. The enhanced corrosion protection ability of the EHPAEK coatings was ascribed to the redox catalytic capabilities of the oligoaniline segment. (C) 2015 Elsevier B.V. All rights reserved.
Conductive Bilayer Polymer Films Formed by Polyaniline and Polymeric Ionic Conductor

QC Gu,HS Xu

DOI: https://doi.org/10.1002/(sici)1097-4628(19971017)66:3<537::aid-app14>3.0.co;2-s

IF: 3

1997-01-01

Journal of Applied Polymer Science

Abstract:Conductive bilayer polymer films based on polymer electrolyte and polyaniline have been prepared by the electrochemical polymerization of aniline on an electrode covered with an ionic conductive polymer film. Electrochemical polymerization was carried out by the potentiodynamic method. The electrochemical properties of the bilayer films were investigated by cyclic voltammetry. The cyclic voltammograms indicated that the bilayer films have good redox stability, as well as reversibility, and show electrochemical activity in the solid state at room temperature. An all-solid-state rechargeable battery composed of lithium and this bilayer polymer film was tested. The preliminary experimental results showed that the battery can discharge in moderate electric current. © 1997 John Wiley & Sons, Inc. J Appl Polym Sci 66: 525–536, 1997
Underpotential electroless deposition of metals on polyaniline

Amrita Singh,Asfiya Contractora,Ravindra D. Kale,Vinay A Juvekar

DOI: https://doi.org/10.48550/arXiv.2006.03635

2020-06-06

Abstract:A novel technique to deposit metals on highly conjugated polyaniline films has been developed. In general, electrodeposition of metals, having low reduction potential, from aqueous solution, is difficult due to disruptive effect of hydrogen which evolves during the process. This difficulty is avoided using conducting polymers films with high surface mass density. The polymer chains of these films possess a high degree of conjugation. Such a polymer produces highly stable polarons and therefore has the ability to perform underpotential deposition. Our method involves reduction of polyaniline film with formic acid followed by dipping the coated electrode in the metal salt solution. Deposition of the metal is monitored by rise in the open circuit potential of the electrode. Deposition of metals with high surface mass density has been achieved. The metal is most likely present in the polymer as a coordination complex with amine nitrogen. Such form of metal is expected to have higher catalytic activity than the zero-valent metal. We have been able to deposit metals such as Mn and Cu. Among these, Mn cannot be deposited on polymer by any other method.

Applied Physics
Electrochemical impedance and morphological characterization of platinum-modified polyaniline film electrodes and their electrocatalytic activity for methanol oxidation

Lin Niu,Qiuhong Li,Fenghua Wei,Xiao Chen,Hao Wang

DOI: https://doi.org/10.1016/S0022-0728(03)00085-8

IF: 4.598

2003-01-01

Journal of Electroanalytical Chemistry

Abstract:The electrochemical impedance spectroscopy of a platinum-modified polyaniline film formed by cycling potential or constant potential deposition of platinum particles in polyaniline film is studied in sulfuric acid solution. The results show that compared with the pure polyaniline film∣H2SO4 solution interface, the deposition of platinum in the polyaniline matrix greatly reduces the electrochemical charge transfer resistance (Rct) in the platinum-modified polyaniline film∣H2SO4 solution interface. The surface morphology of the electrodes is observed by scanning electron microscopy. This shows that the different polarization modes affect the nature of the platinum deposits, such as their size, amount, real surface area and distribution in the polymer matrix. The electrocatalytic activity of platinum-modified polyaniline film electrodes for methanol oxidation is discussed on the basis of platinum loading and real surface area which result from varying electrodeposition modes, such as potential limits in cyclic potential polarization or selected potentials in constant potential polarization. Finally, the relationship between impedance characteristic and electrocatalytic activity has been suggested.
Electro‐Co‐Polymerisation of Polypyrrole‐Polyaniline Composites in Ionic Liquids for Metal‐Free Hydrogen Evolution Electrodes

Chhavi Sharma,Yuvraj Singh Negi,Kaushik Parida,Sara Dale

DOI: https://doi.org/10.1002/open.202400215

2024-09-26

ChemistryOpen

Abstract:Polypyrrole: polyaniline composites in a 1 : 10 ratio were studied for their hydrogen evolution ability and were found to improve after continued cycling in 0.5 M H2SO4 indicating protonation of the conducting polymers to a higher conducting state. Pure organic films consisting of polypyrrole, polyaniline and a composite of polypyrrole and polyaniline electrodeposited in the ionic liquid EMIM‐TFSI onto mesoporous carbon electrodes are tested for their hydrogen evolution reaction capabilities. The use of these intrinsically conducting polymers is seen as a way of stepping away from expensive and rare metallic catalysts. Co‐polymerisation of polypyrrole and polyaniline in a 1 : 10 ratio in EMIM‐TFSI was found to be doped with the TFSI− anion and be much more active to the hydrogen evolution reaction when compared to pure polymers. Tafel analysis of the composite gave a value of 144 mV/dec indicating that the Volmer step is the rate limiting step. However, stability tests showed an improvement in the composite's overpoential performance for the hydrogen evolution reaction.

chemistry, multidisciplinary
Study on the impedance characteristic and electrocatalytic activity of platinum-modified polyaniline film

Lin Niu,Qiuhong Li,Xiao Chen,Fenghua Wei,Hao Wang,Hu Zhang

DOI: https://doi.org/10.1002/jccs.200300165

2003-01-01

Journal of the Chinese Chemical Society

Abstract:The composite electrode of platinum-modified polyaniline film is formed in 0.5 M H2SO4 + 3 mM H2PtCl6 solution by cyclic potential or constant potential deposition of platinum particles in polyaniline film. To make a comparison, the polyaniline film with the same initial thickness and structure is also treated with the cyclic potential or constant potential polarization in 0.5 M H2SO4 solution. The electrochemical impedance spectroscopy (EIS) of the composite electrode of platinum-modified polyaniline film is studied in sulfuric acid solution and compared with the EIS of the polyaniline film without platinum dispersion. The results show that the different modes of potential polarization affect greatly the nature and distribution of the platinum particles, instead of the structure of the polyaniline film (matrix). The electrode reaction kinetics and mass transport process parameters involving charge transfer resistance (R-ct), double layer capacitance (C-dl), constant phase elements (CPE) and Warburg impedance in platinum substrate/platinum-modified polyaniline film/solution interface are discussed on the basis of the interpretation of the characteristic impedance spectra and connected to the electrocatalytic activity on the oxidation of methanol molecules.
Electrosynthesis of Soluble Polyaniline in Acetic Acid

Lin Guo,Gaoquan Shi,Yingqiu Liang

DOI: https://doi.org/10.1007/s002890050418

IF: 2.843

1998-01-01

Polymer Bulletin

Abstract:Summary Aniline has been electropolymerized in acetic acid at a controlled potential of 1.1 V (vs. SCE). The polymer obtained from this system was undoped-like and soluble in many organic solvents such as acetic acid, N-methyl-2-pyrrolidone (NMP), acetonitrile, tetrahydrofuran, methanol, alcohol and acetone. Its electrochemical behavior and structure have been examined by cyclic voltammetry and UV-visible and FT-infrared spectroscopies. The experimental results indicated the polymer has a short and branched structure.
Electrochemical polymerization of 1-naphthylamine and properties of poly-1-naphthylamine

Xiang Li,Na Ta,Cheng Sun

2005-01-01

Abstract:A functional, electrically conducting polymer, poly-1-naphthylamine (PNA), was generated by electrochemical polymerization in a sulfuric acid solution. This product is a blue material soluble in common strongly polar organic solvents such as dimethylsulfoxide, dimethyl formamide and N-methyl-2-pyrrolidone. PNA shows good electrochemical reversibility, stability and unique redox properties in 0.50 mol.dm(-3) Na2SO4 at pH 1.0. Based on FTIR x-ray photoelectron spectral data, a scheme for the mechanism of polymerization is suggested. PNA-modified electrodes exhibit significant electrocatalytic activity for the reduction of H2O2 in 0.1 mol.dm(-3) citrate buffer of pH 5.0. It is hoped that PNA-modified electrodes might be available for practical use for the determination of H2O2.
Palladium electrodeposition from Ammonia-free electrolyte

C.K. Lai,Y.Y. Wang,C.C. Wan

DOI: https://doi.org/10.1016/0022-0728(92)80081-E

IF: 4.598

1992-01-01

Journal of Electroanalytical Chemistry

Abstract:The electrodeposition of palladium from an ammonia-free electrolyte with both direct current and pulse current is discussed. The polarization experiments show that the electrode reactions include oxygen reduction, hydrogen evolution and palladium deposition. The oxygen reduction is always mass transfer-controlled. Deposits obtained with current densities higher than the limiting one are powdery. The current efficiency also drops under these conditions. The variation of the electrode potential during current pulses reveals that hydrogen desorption occurs during pulse-off periods. This hydrogen desorption refreshes the electrode surface and facilitates hydrogen reduction in the next pulse. It explains the severe drop in current efficiency in pulse plating with long pulse-off times. This explanation is also supported by the morphology observations.
Synthesis of Conducting Polyaniline with Photopolymerization Method and Characterization

Siti Veren Joana Sury,Alizar Ulianas,Syamsi Aini

DOI: https://doi.org/10.1088/1742-6596/1788/1/012004

2021-02-01

Journal of Physics: Conference Series

Abstract:Abstract Polymers as they are known as molecules formed by repetition of small molecules known as monomers, polymers that are often used cannot conduct electricity. Along with the development of the polymer era at this time can also conduct electricity known as conductive polymers. One of the conductive polymers that attracts attention is polyaniline. Synthesis of polyaniline conductive polymers is carried out with aniline monomers mixed with Ethylene Glycol Dimetacrylate (EGDMA) as Crosslinkers , and Dimethoxy phenylacetophenone (DMPP) as the initiator. In this reasearch, the polymerization processed with the photopolymerization method with a mixture of Aniline (mL), DMPP (0.1 g), and EGDMA (mL) polymerized with photopolymer. The polymers obtained were tested for electrical conductivity, the composition which showed optimum conductivity was in the ratio of aniline and EGDMA 1 : 1 with the electrical conductivity of 0.001462 Ohm.cm −1 . The conductivity measurement is done by using Four Point Probe (FPP) and other characterization measurements using FTIR (Fourier Transform Infrared) and TGA (Thermo-gravimetric Analysis).
Process for preparing polymeric aluminium chloride through dimensionally stable anodes

Qu Jiuhui,Hu Chengzhi,Liu Huijuan

2005-01-01

Abstract:The invention discloses a process for preparing high grade polymeric aluminium chloride through electrolysis of shape stable anode, wherein aluminium chloride is used as electrolyte, shape stable anode is used as the anode, titanium as cathode, appling DC electricity for a predetermined period of time, and circulating the electrolyte.
Aniline-Naphthylamine Copolymer Integrated with Aluminum Terephthalate-Based Metal Organic Framework for Efficient Hydrogen Evolution From Seawater

Yosef Jazaa,Riyadh Abdulkareem,Linda Mariuxi Flores Fiallos,Shelesh Krishna Saraswat,Sherzod Abdullaev,Rolando Marcel Torres Castillo,Devendra Pratap Rao,Zaid H. Mahmoud,Ali A. Rajhi

DOI: https://doi.org/10.1007/s11665-024-09175-2

IF: 2.3

2024-02-03

Journal of Materials Engineering and Performance

Abstract:A composite made of aniline-naphthylamine copolymer (αNPANI) integrated with an aluminum terephthalate-based metal organic framework (MIL53(Al)) was created by chemically oxidizing aniline monomer in the presence of various contents of naphthylamine and MOF for the hydrogen evolution reaction (HER). There were some nanorods and a microporous structure observed in the SEM images of the copolymer. In the case of the composite (αNPANI/MIL53(Al)), the MOF crystal structures were not visible, suggesting that MOF might be wrapped by the copolymer. The catalytic activities of the prepared electrodes were evaluated in artificial seawater using electrochemical impedance spectroscopy (EIS) and linear sweep voltammetry (LSV) techniques. The Tafel slope values of 98.4, 83.3, and 61.2 mV dec −1 were respectively obtained for the PANI, αNPANI, and αNPANI/MIL53(Al) electrodes. This indicated that the presence of both naphthylamine and MOF in the PANI structure dramatically increased the catalytic H 2 evolution. Chronopotentiometry was used to demonstrate the stability of αNPANI/MIL53(Al), and it was discovered that the produced electrode remained stable for at least 48 h after electrolysis.

materials science, multidisciplinary
Low Potential Electropolymerization Of Anisotropic Conductive Polythiophene Films And Fabrication Of Electrical Devices

XiaoBo Wan,Yun Lu,Xiaorong Liu,Liang Zhou,Shi Jin,Gi Xue

1999-01-01

Chinese Journal of Polymer Science

Abstract:The Complexation of thiophene with a Lewis acid with moderate acidity as a solvent, such as BF3-ethyl ether (BFEE) remarkedly lowered the electrochemical polymerization potential. The positively charged metal surface of electrode in the process of electrochemical deposition enhanced the coordination interaction between pi-electrons of thiophene unit and the metal, which makes thiophene rings lie parallel to the surface of electrode, resulting in a highly ordered polymeric structure. Because of the large intra-chain transfer integrals, the transport of charge is believed to be principally along the conjugated chains, which is much greater than the inter-chain hopping. The specific electrical resistance across the polythiophene film thickness is more than 10(4) times than that along the surface plane of the film. In this paper we review the recent development of polymerization technique by low potential electrochemical method performed in our lab and several electrical devices in which the compact polythiophene films, such as anionic and cationic sieves, and laminate film junction of undoped polythiophene derivatives were used.
Effect of Different Protonic Acid on the Rate of the Electrochemical Polymerization of Aniline

YU Hua-jiang,WU Ke-zhong,WANG Qing-fei,LI Jian-ling

2008-01-01

Abstract:The electrochemical polymerization of aniline were carried out by using the cyclic voltmmetric method in the different protonic acid.The rates measurements of the electrochemical polymerization of aniline demonstrated by the polymer electric quantity depend on cyclic number.The polymerization rate of aniline is strongly affected by concentration.The polymerization of aniline is first order with respect to the concentration of below 7.5 mol/L.The presence of in the aniline solution plays an important role in increasing the polymerization rate.The polymerization of aniline is zero order with respect to the concentration of exceed 7.5 mol/L.Based on the experimental data,a rate equation dealing with the concentration of aniline and is presented at a given acid concentration.The dependence of the polymerization rate of aniline on the concentration of aniline and in the rate equation is in good agreement with the experimental data.
Synthesis and characterization of chloride doped polyaniline by bulk oxidative chemical polymerization.Doping effect on electrical conductivity

Yomen Atassi,Mohammad Tally,Mazen Ismail

DOI: https://doi.org/10.48550/arXiv.0809.3552

2008-09-21

Materials Science

Abstract:Conductive polymers or "organic metals" are highly engineered nanostructured materials made from organic building blocks. They are candidates as molecular wires for nanotechnology applications in molecular electronics. The conduction in these polymers is due to the presence of delocalized molecular orbitals. In this work, we present the synthesis of chloride doped polyaniline by bulk oxidative chemical polymerization using a solid aniline salt as a monomer instead of liquid aniline to diminish toxic hazards. The FTIR and UV-visible spectra confirmed the expected structure of the polymer. The electrical conductivity measured using a four-probe method was 1.7 S/cm. The dependence of impedance modulus on frequency was measured using an HP impedance analyzer in the range 10 kHz-13 MHz. The influence of doping and the preparation temperature on the electrical conductivity were also investigated.

Electrochemical polymerization of anilinium hydrochloride

Poly(olefin)-Based Anion Exchange Membranes Prepared Using Ziegler–Natta Polymerization

Role of the Anilinium Ion on the Selective Polymerization of Anilinium 2-Acrylamide-2-methyl-1-propanesulfonate

Electrosynthesis of poly(aniline-co-p-aminophenol) having electrochemical properties in a wide pH range

Electrochemical Study of a Polypyrrole Film/Decanethiol Self-Assembled Monolayer on a Gold Electrode

Chemical Polymerization Method to Synthesize Polyaniline as a Novel Anode Catalyst in Microbial Fuel Cell

Synthesis and Electrochemical Properties of Electroactive Hyperbranched Poly(Aryl Ether Ketone) Bearing Oligoaniline Segments

Conductive Bilayer Polymer Films Formed by Polyaniline and Polymeric Ionic Conductor

Underpotential electroless deposition of metals on polyaniline

Electrochemical impedance and morphological characterization of platinum-modified polyaniline film electrodes and their electrocatalytic activity for methanol oxidation

Electro‐Co‐Polymerisation of Polypyrrole‐Polyaniline Composites in Ionic Liquids for Metal‐Free Hydrogen Evolution Electrodes

Study on the impedance characteristic and electrocatalytic activity of platinum-modified polyaniline film

Electrosynthesis of Soluble Polyaniline in Acetic Acid

Electrochemical polymerization of 1-naphthylamine and properties of poly-1-naphthylamine

Palladium electrodeposition from Ammonia-free electrolyte

Synthesis of Conducting Polyaniline with Photopolymerization Method and Characterization

Process for preparing polymeric aluminium chloride through dimensionally stable anodes

Aniline-Naphthylamine Copolymer Integrated with Aluminum Terephthalate-Based Metal Organic Framework for Efficient Hydrogen Evolution From Seawater

Low Potential Electropolymerization Of Anisotropic Conductive Polythiophene Films And Fabrication Of Electrical Devices

Effect of Different Protonic Acid on the Rate of the Electrochemical Polymerization of Aniline

Synthesis and characterization of chloride doped polyaniline by bulk oxidative chemical polymerization.Doping effect on electrical conductivity