Abstract:The inorganic powder slurry extrusion printing technique known as robocasting is an interesting method to fabricate complex porous architectures whereby feedstocks containing organic binders and powders are printed and the resulting scaffolds are subjected to sintering. A major limiting factor of this technique is the simultaneous tailoring of vascularization efficacy and osteogenic activity, usually done by adding the secondary phase in the organic slurry before the writing step. Mechanical mixing of biphasic powders is required to avoid compromising the biological performance and physical defects caused by significantly different physicochemical properties. This study addresses this issue by developing a selective ion doping and microstructure tuning for the production of bioceramic scaffolds with a binozzle robocasting process. Different metal ions (Sr2+, Mg2+) were doped into wollastonite (CaSiO3; CSi) powders considering the mechanical stability and bioactive enhancement of the bioceramic scaffolds. Subsequently, the Mg-doped CSi slurries were used as shell-nozzle feedstocks added with 5, 10, and 15 μm diameter polystyrene microbeads that allowed shell-layer micropore production in pore struts during sintering. Finally, the most promising pore-strut microstructures and mechanical evolution of scaffolds were evaluated, and especially the enhanced fibrovascularization potential was confirmed in dorsal muscle embedding model in rabbits. This study may open an avenue to designing multiproperty-tuned macro- and microporous bioceramics for bone regenerative medicine, especially in challenging bone defect conditions.

Multi-directional freeze casting of porous ceramics with bone-inspired microstructure

Bioinspired Large-Scale Aligned Porous Materials Assembled with Dual Temperature Gradients

Effect of Foreign Ion Substitution and Micropore Tuning in Robocasting Single-Phase Bioceramic Scaffolds on the Physicochemical Property and Vascularization

Freeze casting of arbitrary‐shaped porous ceramics

Ultrahigh Strength of Three-Dimensional Printed Diluted Magnesium Doping Wollastonite Porous Scaffolds

3D Long-Range Ordered Porous Ceramics Prepared by a Novel Bidirectional Freeze-Casting Technique

Structure/processing relationships and mechanical properties of freeze-cast B4C scaffolds with unidirectional channels

Multi-directional freeze-casting of interpenetrating phase composites with multi-aligned structure, nearly isotropy, high performance

Hierarchical materials with interconnected pores from capillary suspensions for bone tissue engineering

3D Printing Magnesium-Doped Wollastonite/β-Tcp Bioceramics Scaffolds with High Strength and Adjustable Degradation

3D Printing of Hollow Microspheres into Strong Hierarchical Porous Ceramics

Controlled Porosity Of Ceramic Scaffold By Directional Freeze Casting And Scaffold Printing

Pore Architectures and Mechanical Properties of Porous α-SiAlON Ceramics Fabricated via Unidirectional Freeze Casting Based on Camphene-Templating

The Application of Freeze-casting Method for Fabrication of Calcium Phosphate Biomaterials

Stiff, porous scaffolds from magnetized alumina particles aligned by magnetic freeze casting

Fabrication of Porous Alumina Ceramics with Directional Pore Channels Structure by Freeze-Gel Casting Processing

Pore Architectures And Mechanical Properties Of Porous -Sialon Ceramics Fabricated Via Unidirectional Freeze Casting Based On Camphene-Templating

Ceramics with Special Porous Structures Fabricated by Freeze-Gelcasting: Using tert-Butyl Alcohol as a Template

Three-Dimensional Printing of Cuttlebone-Inspired Porous Ceramic Materials

The controllable microstructure of porous Al2O3 ceramics prepared via a novel freeze casting route