Microstructurally Tailored Thin β‐Ag 2 Se Films toward Commercial Flexible Thermoelectrics
Yan Lei,Ruijuan Qi,Miaoying Chen,Hong Chen,Chengcheng Xing,Fengrui Sui,Longyan Gu,Weiwei He,Yange Zhang,Takahiro Baba,Tetsuya Baba,Hong Lin,Takao Mori,Kunihito Koumoto,Yuan Lin,Zhi Zheng
DOI: https://doi.org/10.1002/adma.202104786
IF: 29.4
2022-01-02
Advanced Materials
Abstract:Aiming to overcome both the structural and commercial limitations of flexible thermoelectric power generators, an efficient room-temperature aqueous selenization reaction that can be completed in air within less than 1 min, to directly fabricate thin β-Ag<sub>2</sub> Se films consisting of perfectly crystalline and large columnar grains with both in-plane randomness and out-of-plane [201] preferred orientation, is designed. A high power factor (PF) of 2590 ± 414 µW m<sup>-1</sup> K<sup>-2</sup> and a figure-of-merit (zT) of 1.2 ± 0.42 are obtained from a sample with a thickness of ≈1 µm. The maximum output power density of the best 4-leg thermoelectric generator sample reach 27.6 ± 1.95 and 124 ± 8.78 W m<sup>-2</sup> at room temperature with 30 and 60 K temperature differences, respectively, which may be useful in future flexible thermoelectric devices.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology