Abstract:Continuous carbon fiber (CF)-reinforced poly (ether ether ketone) (PEEK) composites have excellent mechanical properties, but their processing techniques are limited. Therefore, we promoted a braiding method based on the hybrid fiber method by hot-compacting CF/PEEK plain weave fabrics to solve the problem of difficult wetting between CF and PEEK. Four parameters—melting temperature, molding pressure, crystallization temperature and the resin contents—were investigated for optimized fabrication. After studying the melting range, thermal stability and the contact angle of PEEK under different temperatures, the melting temperature was set at 370 °C. An ultra-depth-of-field 3D microscope was adopted to investigate the effects of molding pressure in the melting stage. The tensile strength or modulus along and perpendicular to the carbon fiber direction and crystallinity under different crystallization temperatures were analyzed. As a result, the sample crystalized at 300 °C showed an excellent tensile properties and crystallinity. The increased mass ratio of PEEK ranging from 50.45% to 59.07% allowed for much stronger interfacial strength; however, the higher resin content can lead to the dispersion of CFs, loss of resin and the formation of defects during processing. Finally, the optimal resin mass content was 59.07%, with a tensile strength of 738.36 ± 14.49 MPa and a flexural strength of 659.68 ± 57.53 MPa. This paper studied the optimized processing parameters to obtain better properties from CF/PEEK plain weave fabrics and to further broaden the specific applications of CF/PEEK composites, demonstrating a new direction for its fabrication.

Lubricious yet tough fabric composites at cryogenic temperature by sulfonated polyether-ether-ketone reinforcement

Lubricating Performance of Polytetrafluoroethylene Hybrid Fabric Composites with Removed Thermosetting Resin at Cryogenic Temperatures

Tribological Properties of PTFE-based Fabric Composites at Cryogenic Temperature

Construction of a PTFE-based lubricant film on the surface of Nomex/PTFE fabric to enhance the tribological performance at cryogenic temperatures

Carbon Fibre Reinforced Bisphenol-a Type SPEEK Composite for Water Lubricated Superlubricity

Tribological properties of PTFE/Kevlar fabric composites under heavy loading

In-situ observation of transfer film formation and evolution for the fabric composite lubricated spherical plain bearing at cryogenic and wide temperature range

Role of transfer film formation on the tribological properties of polymeric composite materials and spherical plain bearing at low temperatures

Synergistic Enhancement of the High-Temperature Friction and Wear Behavior of PTFE Matrix Composites with the Addition of CF, PEEK, and TiC

Tribological Performance Study of Low-Friction PEEK Composites under Different Lubrication Conditions

Tribological behavior of modified polyetheretherketone composites in sliding against stainless steel under water lubrication

Enhanced high‐temperature tribological performance of PTFE / PI fabric composites by simultaneously introducing PDA / SiO 2 hybrid coating and aramid product reinforcements

Tensile and tribological properties of polytetrafluroethylene homocomposites

Tribological behavior of PTFE/Nomex/phenolic composite lubricant under cold forming condition in the bearing assembly process

Wear resistant PEEK composites with great mechanical properties and high thermal conductivity synergized with carbon fibers and h‐BN nanosheets

Tailoring Polyimide Composites with Low Friction and Wear at High Temperatures

A Study on the Mechanical and Tribological Properties of Carbon Fabric/PTFE Composites

Tribological Properties of PEEK and Its Composite Material under Oil Lubrication

The Optimization of Process Parameters and Characterization of High-Performance CF/PEEK Composites Prepared by Flexible CF/PEEK Plain Weave Fabrics

Cryogenic properties of PEG/nano-SiO2 co-toughened winding resin and its carbon fiber-reinforced composites

Effect of basalt fiber on tribological and mechanical properties of polyether-ether-ketone (PEEK) composites