Abstract:Dense polycrystalline LiTaO3 (LTO) ceramics have rarely been reported due to their poor sinterability, although LTO single crystals are among the well-known piezoelectric and ferroelectric. In this study, LiTaO3-based ceramics with 3 wt% and 5 wt% MnO2 (referred to 3MLT and 5MLT, respectively) are prepared by pressure-less sintering at different temperatures of 1200 degrees C, 1250 degrees C, 1300 degrees C and 1350 degrees C, respectively, and the effects of sintering temperature on the sinterability, microstructure development and dielectric properties are investigated. The sintered density of the LiTaO3 -based ceramics increases significantly at first with increasing of sintering temperature, and then decreases afterwards. Sintered densities of -92.6% and 93.1% were achieved for 3MLT and 5MLT sintered at 1250 degrees C, respectively, and both compositions show a rather homogeneous and well-developed grained microstructure. A moderate amount of MnO2 was entered into the LiTaO3 lattice to form a solid solution, however, Mn3O4 was formed at the grain boundaries and junctions when excess amount of MnO2 added, where the solid solubility is dependent on the sintering temperature. The dielectric properties of both 3MLT and 5MLT ceramics, studied as a function of frequency, show a strong dependence on sintering temperature, where the dielectric constant increases first and then decreases with the increasing of sintering temperature. The dielectric loss first decreases and then increases with the increasing of sintering temperature. Both 3MLT and 5MLT demonstrate a maximum in dielectric constant when sintered at 1250 degrees C and 1350 degrees C, respectively. The lowest dielectric loss could be obtained at 1250 degrees C, which was selected as the optimum sintering temperature for both compositions. (C) 2020 Elsevier B.V. All rights reserved.

Temperature-dependent dielectric and wide-temperature-range microwave absorption properties of La0.8Sr0.2MnO3/Al2O3–13%TiO2 coatings

Temperature-dependent dielectric properties and high-temperature microwave absorption performance of Ti3SiC2/Al2O3-13%TiO2 coatings

The dielectric behavior and efficient microwave absorption of doped nanoscale LaMnO3 at elevated temperature

Temperature-dependent Optical Properties of Low-Loss Plasmonic SrMoO3 Thin Films

Thermally stable ultra-thin and refractory microwave absorbing coating

Rational Design of a Core-Shelled Ti3AlC2@La2Zr2O7 Composite for High-Temperature Broadband Microwave Absorption

The dielectric and microwave absorption properties variation with temperature of La0.5Sr0.5CoO3 ceramics and improved microwave absorption by FSS

Polycrystalline La0.845Sr0.155MnO3:Ag ceramics (0 ≤ x ≤ 0.5) with room-temperature TCR and MR for improved uncooling photoelectric and magnetic devices

Low Thermal Conductivity Sr 2+ , Zn 2+ and Ti 4+ Ions Co-Doped LaMgAl 11 O 19 for Potential Thermal Barrier Coating Applications

Temperature-insensitive and enhanced microwave absorption of TiB2/Al2O3/MgAl2O4 composites: Design, fabrication, and characterization

Microwave Absorption Investigations of LSMO/SiO2 Composite Material at Different Temperatures

MnO2 As an Effective Sintering Aid for Difficult-to-sinter LiTaO3-based Ceramics: Densification and Dielectric Properties

Tunable thermo-optical performance promoted by temperature selective sputtering of titanium oxide on MgO-ZrO2 coating

Dual properties of microwave absorption and thermal protection in La0.5Sr0.5FeO3‐Al2O3 pseudo‐binary composites

Research Progress of High Temperature Microwave Absorption Materials

Emissivity of La1-xSrxMnO3/acrylic Resin Thermal Control Coating

Absorption of Microwaves in La1−xSrxMnO3 Manganese Powders over a Wide Bandwidth

Low-field Magneto-Transport Property of La0.5Sr0.5MnO3 Thin Films Deposited at Low Temperature by Laser Ablation

Electromagnetic and Microwave Absorption Performance of Some Transition Metal Doped La0.7Sr0.3Mn1−xTMxO3±δ (tm=fe, Co or Ni)

Plasma-induced FeSiAl@Al2O3@SiO2 Core–shell Structure for Exceptional Microwave Absorption and Anti-Oxidation at High Temperature

Effect of Oxidation on the Microwave Absorption Properties of Rare-Earth Intermetallics La2Fe4Co10B