Abstract:Over the last few years, there has been a high interest in increasing the energy density of lithium-ion batteries in order to increase the driving range of battery electric vehicles. On a material level, silicon is a promising anode active material candidate due to its high theoretical capacity of 3579 mAh g -1 , which is approximately ten-fold higher than that of the currently used graphite anodes with a theoretical capacity of 372 mAh g -1 . [1] However, the main drawbacks of silicon are its intrinsic volume expansion of +300 % upon lithiation. [2] This leads to rupturing of the passivating solid electrolyte interphase (SEI), particle cracking, and loss of electronic contact, limiting the lifetime of batteries with silicon based anodes, thus hindering their transition into application. As a possible solution, Jantke et al. proposed the concept of partial utilization of μm-sized crystalline silicon, where only one-third of the theoretical capacity is used for (de)lithiation. Thereby, a crystalline core remains, and the volume expansion on the particle-level is reduced to approximately + 100%. [3] In addition, it was shown that irreversible losses during the formation and upon cycling can be compensated by pre-lithiation of the anode, which increases the lifetime significantly. [4,5] In this study, we investigated a promising cell chemistry for high-energy applications, containing a Si-dominant anode and a cathode based on a Co-free lithium- and manganese-rich NMC. The here used anode consists of 70 wt% silicon, 20 wt% graphite, 2 wt% conductive C65, and 8 wt% LiPAA-binder. Note that graphite mainly acts as a conductive additive within the operating voltage window, with a negligible contribution to the overall anode capacity. The electrochemical testing was conducted at 25 °C in Swagelok ® T-cells containing two glass fiber separators, a 1M LiPF 6 in FEC:DEC (2:8, v:v) electrolyte and a lithium metal reference. Without pre-lithiation, these full-cells suffered from rapid capacity fading, reaching the 80 % state-of-health (SOH) criterion after ~100 cycles. As will be discussed, our analysis shows that the primary mode of failure in these cells is the loss of cyclable lithium, evidenced by an increase in the end-of-discharge potential at the anode. It was found that with increasing end-of-discharge potential at the anode, the anode resistance at low state-of-charge rises significantly. Therefore, silicon anodes were lithiated in coin half-cells to 25, 50, and 75 % of the reversible cathode capacity (corresponding to 300, 600, and 900 mAh g Si -1 ). Then, the anodes were harvested in the lithiated state and assembled in a Swagelok ® T-cell with the same cathode, separator, and electrolyte as the non-pre-lithiated reference cells. Pre-lithiation leads to similar reversible charge/discharge capacities, but generates a cyclable lithium reservoir in the anode. Successively increasing the pre-lithiation of the anode increases the lifetime from 100 to 550 cycles. The onset of the above-described aging phenomena is delayed by 150 cycles for every additional 25 % pre-lithiation. Further, the influence of aging and lithium inventory on anode and cathode resistance will be discussed, showing that the increase in anode resistance is mainly a function of (de)lithiation rather than cycle number. Acknowledgments: The authors gratefully acknowledge the funding from the BMBF (Federal Ministry of Education and Research, Germany) in the ExZellTUM III project (grant number 03XP0255). We also kindly thank Wacker Chemie AG and BASF SE for providing the anode and cathode active materials. References: [1] M. N. Obrovac, L. Christensen, Electrochem. Solid-State Lett. 2004 , 7 , A93–A96. [2] M. N. Obrovac, V. L. Chevrier, Chem. Rev. 2014 , 114 , 11444–11502. [3] D. Jantke, R. Bernhard, E. Hanelt, T. Buhrmester, J. Pfeiffer, S. Haufe, J. Electrochem. Soc. 2019 , 166 , A3881–A3885. [4] S. Haufe, R. Bernhard, J. Pfeiffer, J. Electrochem. Soc. 2021 , 168 , 080531. [5] V.L. Chevrier, L. Liu, R. Wohl, A. Chandrasoma, J. A. Vega, K. W. Eberman, P. Stegmaier, E. Figgemeier, J. Electrochem. Soc. 2018 , 165 , A1129–A1136.

Delineating the Effects of Transition‐Metal‐Ion Dissolution on Silicon Anodes in Lithium‐Ion Batteries

Insights into the Crossover Effects in Cells with High‐Nickel Layered Oxide Cathodes and Silicon/Graphite Composite Anodes

Simultaneously Manipulating Carbon Coating Layers and Void Structures in Silicon/Carbon Anode Materials Via Bifunctional Templates for Lithium-Ion Batteries

Artificial Solid Electrolyte Interphase to Address the Electrochemical Degradation of Silicon Electrodes

Impact of Electrolyte on Direct-Contact Prelithiation of Silicon-Graphite Anodes in Lithium-Ion Cells with High-Nickel Cathodes

Tailoring chemical composition of solid electrolyte interphase by selective dissolution for long-life micron-sized silicon anode

Effects of Lithium Polysulfides on the Formation of Solid Electrolyte Interfaces in Silicon Anodes

Tailoring Stress and Ion-Transport Kinetics Via a Molecular Layer Deposition-Induced Artificial Solid Electrolyte Interphase for Durable Silicon Composite Anodes

Elucidating the Effect of Pre-Lithiation of Silicon Dominant Anodes on the Full Cell Performance

Destructive effects of transitional metal ions on interfacial film of carbon anode for lithium-ion batteries

Incorporation of lithium oxide into silicon anode via magnetron co-sputtering to optimize structural stability and cycling performance

Study on the Application of Ailicon-Cobalt Oxide Anode Material in Lithium-Ion Batteries

Lithium Silicates in Anode Materials for Li-Ion and Li Metal Batteries

The Effect of Silicon Nanoparticle Size on Cycle and Calendar Life

The Role of Silicon in Silicon-Graphite Composite Electrodes Regarding Specific Capacity, Cycle Stability, and Expansion

Unveiling Electrochemical Properties of Silicon for Stable Cycling Performance of Silicon Anode Materials

Understanding the Effect of Lithium Nitrate as Additive in Carbonate-Based Electrolytes for Silicon Anodes

S-containing and Si-containing compounds as highly effective electrolyte additives for SiOx -based anodes/NCM 811 cathodes in lithium ion cells

Study on Solid Electrolyte Interphase Excessive Growth Caused by Mn (II) Deposition on Silicon Anode

Regulating Anode‐electrolyte Interphasial Reactions by Zwitterionic Binder Chemistry in Lithium‐ion Batteries with High‐nickel Layered Oxide Cathodes and Silicon‐Graphite Anodes

Doped and reactive silicon thin film anodes for lithium ion batteries: A review