Influence of Mo micro-particles on crack formation, microstructure, and mechanical behaviour of laser powder bed fusion fabricated CuZrAl bulk metallic glass composites
Pei Wang,Yang Lei,Jiang Ma,Kaikai Song,Liang Deng,Zhiyuan Liu,Zhangwei Chen,Xufei Liu,Parthiban Ramasamy,Jürgen Eckert
DOI: https://doi.org/10.1080/17452759.2023.2224307
IF: 10.6
2023-06-23
Virtual and Physical Prototyping
Abstract:In this work, a new design principle, i.e. doping with refractory metal particles with a low diffusion rate to prevent the formation of cracks and to improve the mechanical properties of bulk metallic glass (BMG) composites, was put forward. It was proven that crack-free and dense Mo (p) /Cu 47 Zr 47 Al 6 BMG composites with enhanced mechanical properties can be produced via LPBF. The dislocations generated in the Mo particles can release thermal stress, thereby inhibiting the formation of thermal-cracks. The fracture patterns of Mo particles show that they can delay rapid of crack expansion, thereby improving the inherent strength and toughness of the material.
engineering, manufacturing,materials science, multidisciplinary