Effect of UHPC strengthening layer on static and fatigue performance of upper cutouts in orthotropic steel decks

Yang Wang,Junhui Cao,Xudong Shao,Qiyuan Mao,Zhihao Qu,Yang Wang,Junhui Cao,Xudong Shao,Qiyuan Mao,Zhihao Qu

DOI: https://doi.org/10.1016/j.jcsr.2022.107557

IF: 4.349

2022-11-01

Journal of Constructional Steel Research

Abstract:Cutouts are usually used in orthotropic steel decks (OSDs) of bridges and subject to complex stresses under loads. This research performed experimental and theoretical investigations to evaluate the effect of a thin UHPC layer on the fatigue performance of upper cutouts in OSDs. A full-scale specimen was fabricated and tested under static and fatigue loads before and after the specimen was strengthened with the UHPC layer. The results show that a fatigue crack initiated from the weld toe at the upper cutout after 1.15 million cycles of fatigue load with a load range of 216 kN. The use of the UHPC layer generated a steel-UHPC composite specimen subject to an extra fatigue loading for 2 million cycles with the same load range. The propagation length of the fatigue crack was only 1.2 mm, and the propagation rate was reduced from 0.61 × 10−4 mm/cycle to 0.0095 × 10−4 mm/cycle, with a reduction of 98.4%. The peak stress at the crack tip decreased from 139.0 MPa to 51.6 MPa, by 62.9%. A series of finite element analyses was performed to evaluate the fatigue damage. It was found that the use of the UHPC layer significantly reduced fatigue damage in the fatigue-prone detail around the upper cutouts and extended the fatigue life accordingly.

construction & building technology,engineering, civil