The effects of the solution reactant concentration and temperature on the preparation of Pr 3+ :BaF 2 transparent ceramics

Xinwen Liu,Zhiwei Zhou,Weiwei Li,Yu Yang,Bingchu Mei

DOI: https://doi.org/10.1111/jace.17817

IF: 4.186

2021-04-14

Journal of the American Ceramic Society

Abstract:<p>Barium fluoride (BaF₂) crystals are attracting much attention as efficient inorganic scintillator promising for high‐energy physics, industrial inspection, and other fields because of the fast component of the decay time (0.6 ns) and high radiation resistance. However, two major drawbacks limit its practical application: (i) a slow decay time of ~ 600 ns is derived from self‐trapping excitons; (ii) the absolute light yield from the fast luminescence component is not competitive. The introducing of rare earth ions and preparation of BaF₂ polycrystalline ceramics is considered to be effective measures to solve these bottlenecks. Pr³⁺ is extremely suitable as the activated ion of scintillation materials, which possess emission peaks located in visible band and the faster 5d‐4f transition. In this work, highly sinterable Pr³⁺:BaF₂ precursor powder were synthesized via the co‐precipitation method by adjusting the reactant concentration and temperature. The morphology and microstructure of as‐synthesized powders were characterized using SEM and TEM analysis. The 5 at.% Pr³⁺:BaF₂ transparent ceramic with a transmittance of 50.7% at the wavelength of 500 nm was fabricated by hot pressing the as‐prepared powders at 900℃ for 4h under the axial pressure of 50 MPa. The SEM images of ceramic cross‐section show that the residual pore is the main light scattering source. The absorption and emission spectrum of ceramic samples were discussed.</p>

materials science, ceramics