Abstract:In this work, a calibration of ruby, samarium-doped strontium tetraborate (Sm2+: SrB4O7), and samarium-doped yttrium aluminum garnet (Sm3+: YAG) using Raman and fluorescence spectra was conducted within the temperature range of 296–850 K and pressure range of 0–55 GPa. The obtained calibration can be applied independently for high-temperature or high-pressure conditions and described as the unit form of P = (A′/B′) × [(λ/λT)B′ − 1] with A′ = A (296 K) + A1 × (T − 296) + A2 × (T − 296)2, B′ = B(296 K) + B1 × (T – 296), and λT = λT (296 K) + ΔλT, where the specific parameters are provided in the main text. It was observed that for the λ1 line (5D0 → 7F0 transition, about 685.2 nm under ambient conditions, also known as the 0-0 line) of Sm2+: SrB4O7, the neglect of the temperature effect on the pressure coefficient may lead to an underestimation of pressure above 35–40 GPa, with a maximum deviation of approximately 2.5 GPa within the range of 55 GPa and 850 K. For Sm3+: YAG, it may introduce significant errors under the whole high temperature and high pressure range if the effect of temperature is ignored, that is, about 3.9 GPa for Y1 line (4G5/2 → 6H7/2 transition, about 617.8 nm under ambient conditions) and 4.6 GPa for Y2 line (4G5/2 → 6H7/2 transition, about 616.0 nm under ambient conditions) at 850 K. Comparing the three fluorescence pressure sensors, the ruby has the strongest signal intensity and highest temperature sensitivity, and the Sm2+: SrB4O7 and the Sm3+: YAG possess lower temperature sensibility, wider used temperature range, and better spectral quality under high temperature and high pressure (HTHP), especially Sm2+: SrB4O7, which has a sharp high-intensity single peak λ1, perhaps the most promising sensor for high P–T experiments. Therefore, in view of the potential deflections of fluorescence peaks of each pressure sensor under HTHP, we recommend utilizing the HTHP-corrected relationships for pressure calibration.

Fluorescence and absorption of Rhodamine 6G solutions as pressure standards for a diamond-anvil cell

Raman Spectra Based Pressure Calibration of the Non-Gauge Sapphire Anvil Cell at High Temperature and High Pressure

Hydrostaticity of pressure-transmitting media for high pressure infrared spectroscopy

Invited article: High-pressure techniques for condensed matter physics at low temperature

Srb4o7:Sm2+: an Optical Sensor Reflecting Non-Hydrostatic Pressure at High-Temperature And/Or High Pressure in A Diamond Anvil Cell

Specific Volume Measurements of Cu, Mo, Pd, and Ag and Calibration of the Ruby R1 Fluorescence Pressure Gauge from 0.06 to 1 Mbar

Fluorescence pressure sensors: Calibration of ruby, Sm2+: SrB4O7, and Sm3+: YAG to 55 GPa and 850 K

Hydrogen Bonding and Dynamics of Methanol by High-Pressure Diamond Anvil Cell Nmr

Permanent Densification of Silica Glass for Pressure Calibration Between 9 and 20 GPa at Ambient Temperature

Procedure for loading diamond cells with high‐pressure gas

High-Pressure Ruby and Diamond Fluorescence: Observations at 0.21 to 0.55 Terapascal

Frequency-resolved Transient Absorption Spectroscopy for High Pressure System

High-pressure fluorescence measurements using a diamond anvil cell (DAC)

Calibration of manganin pressure gauge for diamond-anvil cells

Calibration of the Ruby Pressure Gauge to 800 Kbar under Quasi‐hydrostatic Conditions

High pressure Raman spectroscopy investigation on acetonitrile and acetonitrile–water mixture

Pressure Tuning Dual Fluorescence of 4-(N,n-dimethylamino)benzonitrile

Fluorescence Mechanism of Diamond and the Significance in High Pressure Raman Spectrometry

In situ synchrotron X-ray diffraction with laser-heated diamond anvil cells study of Pt up to 95 GPa and 3150 K

All-optical method to directly measure the pressure-volume-temperature equation of state of fluids in the diamond anvil cell

Ruby Fluorescence Pressure Scale: Revisited