Abstract:In this work, a calibration of ruby, samarium-doped strontium tetraborate (Sm2+: SrB4O7), and samarium-doped yttrium aluminum garnet (Sm3+: YAG) using Raman and fluorescence spectra was conducted within the temperature range of 296–850 K and pressure range of 0–55 GPa. The obtained calibration can be applied independently for high-temperature or high-pressure conditions and described as the unit form of P = (A′/B′) × [(λ/λT)B′ − 1] with A′ = A (296 K) + A1 × (T − 296) + A2 × (T − 296)2, B′ = B(296 K) + B1 × (T – 296), and λT = λT (296 K) + ΔλT, where the specific parameters are provided in the main text. It was observed that for the λ1 line (5D0 → 7F0 transition, about 685.2 nm under ambient conditions, also known as the 0-0 line) of Sm2+: SrB4O7, the neglect of the temperature effect on the pressure coefficient may lead to an underestimation of pressure above 35–40 GPa, with a maximum deviation of approximately 2.5 GPa within the range of 55 GPa and 850 K. For Sm3+: YAG, it may introduce significant errors under the whole high temperature and high pressure range if the effect of temperature is ignored, that is, about 3.9 GPa for Y1 line (4G5/2 → 6H7/2 transition, about 617.8 nm under ambient conditions) and 4.6 GPa for Y2 line (4G5/2 → 6H7/2 transition, about 616.0 nm under ambient conditions) at 850 K. Comparing the three fluorescence pressure sensors, the ruby has the strongest signal intensity and highest temperature sensitivity, and the Sm2+: SrB4O7 and the Sm3+: YAG possess lower temperature sensibility, wider used temperature range, and better spectral quality under high temperature and high pressure (HTHP), especially Sm2+: SrB4O7, which has a sharp high-intensity single peak λ1, perhaps the most promising sensor for high P–T experiments. Therefore, in view of the potential deflections of fluorescence peaks of each pressure sensor under HTHP, we recommend utilizing the HTHP-corrected relationships for pressure calibration.

Ruby Fluorescence Pressure Scale: Revisited

High-Pressure Ruby and Diamond Fluorescence: Observations at 0.21 to 0.55 Terapascal

Invited article: High-pressure techniques for condensed matter physics at low temperature

Fluorescence Mechanism of Diamond and the Significance in High Pressure Raman Spectrometry

Pressure Distribution in the Diamond Anvil Press and the Shear Strenght of Fayalite

Deviatoric Stress In A Quasi-Hydrostatic Diamond-Anvil Cell - Effect On The Volume-Based Pressure Calibration

Calibration of the Ruby Pressure Gauge to 800 Kbar under Quasi‐hydrostatic Conditions

Raman Spectra Based Pressure Calibration of the Non-Gauge Sapphire Anvil Cell at High Temperature and High Pressure

High-pressure fluorescence measurements using a diamond anvil cell (DAC)

Coherent diffraction imaging of nanoscale strain evolution in a single crystal under high pressure

The Application of Synchrotron Radiation in the Research of Mineral Structure under High Pressure

Measurement of Stress in Diamond Anvils with Micro‐raman Spectroscopy

Specific Volume Measurements of Cu, Mo, Pd, and Ag and Calibration of the Ruby R1 Fluorescence Pressure Gauge from 0.06 to 1 Mbar

X-Ray Imaging Of Stress And Strain Of Diamond, Iron, And Tungsten At Megabar Pressures

Fluorescence pressure sensors: Calibration of ruby, Sm2+: SrB4O7, and Sm3+: YAG to 55 GPa and 850 K

In Situ High-Pressure X-ray Diffraction of Natural Topaz

Size Dependence of Cubic to Trigonal Structural Distortion in Silver Micro- and Nanocrystals under High Pressure

Quasi-hydrostatic Compression of Ruby to 500 Kbar

X-ray diffraction of ruby (Al2O3:Cr3+) to 175 GPa

A Focusing System for X-ray Diffraction Studies of Materials under High Pressure in the Diamond Cell

Two-dimensional Energy Dispersive X-Ray Diffraction at High Pressures and Temperatures