Non-Arrhenius Ionic Conductivity Behaviour in Antiperovskite Solid Electrolytes for Sodium Metal Batteries
Brigita Darminto,Mauro Pasta,Hyeon Jeong Lee,Hua Guo,Gregory J. Rees,John Cattermull,Maria Diaz‐Lopez,Kenjiro Hashi,Naoaki Kuwata,Andrew L. Goodwin
DOI: https://doi.org/10.1149/ma2023-02462267mtgabs
2023-01-01
Abstract:Solid-state sodium metal batteries have been proposed as an alternative to lithium-ion batteries (LIBs) for next-generation applications due to the high abundance and wide distribution of sodium resources. 1 Sodium antiperovskites (Na 3 OX, X = Cl, Br, or BH 4 ) have recently attracted great interest as solid electrolyte candidates due to the relatively low processing temperature (<500 o C), reasonable ionic conductivity (up to 4.4 x 10 -3 S cm -1 at room temperature), and great chemical stability against sodium metal anodes. 2,3 Typical solid-state ionic conductors have temperature-dependent ionic conductivity that follows Arrhenius behaviour over a broad range of temperatures, corresponding to a constant activation energy E a . However, this is not the case in Na 3 OBr, and instead a phenomenon resulting in a higher ionic conductivity and lower activation energy is observed to occur at 255 o C. Similar non-Arrhenius ionic conductivity phenomenon has also been reported in the potassium antiperovskite K 3 OI. It has been proposed that this behaviour originated from anion disordering, but conclusive experimental evidence to support this claim has not been reported. 4 An understanding of the origin of this behaviour could enable the synthesis route to be optimised such that higher ionic conductivities could be achieved. In this work, we combined temperature-resolved bulk and local characterisation methods including Pawley and Rietveld refinements of synchrotron x-ray diffraction (XRD), pair distribution function (PDF), solid-state nuclear magnetic resonance (NMR) spectroscopy, and electrochemical impedance spectroscopy (EIS) to gain an insight into the origin of this non-Arrhenius behaviour. We found that this phenomenon does not originate from anion disordering, as previously speculated, because the lattice parameter of Na 3 OBr changed linearly with temperature and no major intensity changes were observed in the Na-Br and Na-O signals in the PDF patterns. Other supporting findings that lead us to this conclusion will be discussed in the presentation. References Wang, X. et al. Ultra-stable all-solid-state sodium metal batteries enabled by perfluoropolyether-based electrolytes. Nat. Mater. 21 , 1057–1066 (2022). Zheng, J., Perry, B. & Wu, Y. Antiperovskite Superionic Conductors: A Critical Review. ACS Mater. Au 1 , 92–106 (2021). Sun, Y. et al. Rotational Cluster Anion Enabling Superionic Conductivity in Sodium-Rich Antiperovskite Na3OBH4. J. Am. Chem. Soc. 141 , 5640–5644 (2019). Zheng, J. et al. Antiperovskite K3OI for K-Ion Solid State Electrolyte. J. Phys. Chem. Lett. 12 , 7120–7126 (2021).