Mechanically Robust, Antibacterial, and Biocompatible Brushite-SiC-Graphene nanoplatelets via mechanochemical solid-state reaction for Bone Tissue Engineering Applications

Lamiaa G. Alharbe

DOI: https://doi.org/10.1016/j.matchemphys.2024.130194

IF: 4.778

2024-12-08

Materials Chemistry and Physics

Abstract:Brushite combined with Silicon carbide (SiC) and graphene nanoplatelets (G) in a ternary nanocomposite via a mechanochemical approach was investigated for its potential application in bone regeneration. Brushite-SiC-G exhibited a synergistic effect of its constituents which demonstrates relatively high mechanical properties (tensile strength: 73.43 ± 1.37 GPa, Young's modulus: 413.58 ± 16.3 GPa) compared to Brushite and Brushite-SiC. Furthermore, Brushite-SiC-G displayed a tailored Ca 2 + ion release profile with an initial lag followed by sustained release (2.3 ± 0.7 ppm at 16 hours. In addition, the presence of graphene in Brushite-SiC-G contributed to remarkable antibacterial activity against P. aeruginosa with a Zone of inhibition (ZOI) value around 13.3 ± 0.7 mm, E. coli around 12.4 ± 1.1 mm), and S. aureus around 11.8 ± 0.9 mm. In vitro studies revealed promising biocompatibility of Brushite-SiC-G with higher cell viability (63% at 2500 μg/mL) compared to Brushite and Brushite-SiC. Moreover, structural investigation by X-ray diffraction (XRD) analysis of Brushite-SiC-G revealed a decrease in Brushite crystallinity (average crystallite size around 400 nm) and microstrain (1.6 x 10−3) compared to pristine Brushite. Scanning electron microscopy (SEM) provided further insights into the morphology of Brushite-SiC-G. The composite exhibited spherical SiC particles with a size range of 70 nm to 600 nm embedded within a Brushite matrix with a 2.30 g/cm3 density. Furthermore, chemical and elemental analyses were carried out by Raman and FTIR, where D and G bands of G were detected. This investigation indicates the ability of Brushite to be reinforced by SiC and G nanoplatelets to be enhanced for biomedical applications.

materials science, multidisciplinary