High union dyeing and fixation rate of cotton/modal blended fabrics via union dyeing with fiber swelling agents

Li, Yongqiang

DOI: https://doi.org/10.1007/s10570-024-06175-2

IF: 6.123

2024-09-21

Cellulose

Abstract:To meet the needs of consumers for high-quality textiles, the blended fabrics gradually become the mainstream of the market. However, developing the union dyeing blended fabrics in finished fabrics is still challenging. In this paper, different mass fractions of urea, caustic soda, ethylenediamine, and ethylenediamine + urea + water fiber swelling agent were used to modify the blended fabric. The barium values for the two fibers, adsorption swelling time and temperature were measured. The results showed that ethylenediamine + urea + water displayed the best combination candidates for the union dyeing of the blended fabric, which had a certain degree of elimination of crystallinity on cotton fibers. The optimal swelling process parameters of ethylenediamine:urea:water were 75:15:10, the temperature is 30 °C, and the time is 90 min. Under this process, washing under different conditions had a significant effect on the union dyeing of the blended fabric. After the fabric was washed with alcohol, the cotton fiber configuration also changed from cellulose type I to cellulose type I (12) + EDA-I (88), with a high degree of transformation and a high degree of decrystallization (30.98%). The modal fiber configuration changed from cellulose type II to cellulose type II (77) + EDA- II (23), with a low degree of transformation and a low degree of decrystallization (8.83%).Finally, the union dyeing values were increased from 0.4 ~ 0.5 to 0.85 ~ 1.1 without.the change of style and feel of the blended fabric. Notably, the breaking strength of the blended fabrics was reinforced. This work has significant implications for the development of high-quality cotton/modal blended fabrics with high union dyeing and fixation rate.

materials science, textiles,polymer science, paper & wood