Simultaneous and Efficient Removal of Oleophilic and Hydrophilic Stains from Polyurethane by the Combination of Easy-Cleaning and Self-Cleaning
Zheng Fang,Junfeng Zhang,Xuefeng Yan,Lizhen Hu,Lin Lei,Huiqing Fan,Weijia Wang,Qi Zhong,Peter Müller-Buschbaum
DOI: https://doi.org/10.1021/acsami.2c01042
2022-04-04
Abstract:The simultaneous and efficient removal of oleophilic and hydrophilic stains from polyurethane (PU) is realized by combining the easy-cleaning from the hydrophilic thermoresponsive hydrogel coating containing acrylamide (AAm), gum arabic (GA), and (ethylene glycol) methyl ether methacrylate (OEGMA300) P(GA/AAm/OEGMA300) and the self-cleaning from the embedded nonmetallic photocatalyst g-C3N4. Due to the existence of strong hydrogen bonds between the hydroxyl groups in the hybrid hydrogel coating and the hydroxyl/carboxyl groups in the plasma-treated PU, the hybrid hydrogel coating is very stable on PU. Simultaneously, the acrylamide network in the hybrid hydrogel coating enhances its mechanical strength. Because the transition temperature of OEGMA300 is well above the room temperature, the cross-linked coating remains hydrophilic in ambient conditions. Thus, oleophilic stains, such as oil and grease, can be easily removed from the coating surface. In addition, the embedded photocatalyst g-C3N4 in the hybrid hydrogel coating introduces the extra capability of decomposing organic compounds under sunshine, which favors the removal of hydrophilic stains such as dyes and wines. After sunlight illumination and simply rinsing with water, both hydrophilic and oleophilic stains can be easily removed. Moreover, this joint cleaning performance can work for a long time. Even after four consecutive cycles, both the easy-cleaning to oleophilic stains by the hydrophilic hydrogel surface and self-cleaning to the hydrophilic stains by the embedded g-C3N4 remain unchanged.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c01042.ATR-FTIR spectra of P(GA/AAm/OEGMA300) hydrogel coating on PU and on silicon substrate; infrared thermographic images of PU cross-linked with P(GA/AAm/OEGMA300)/g-C3N4 (2 wt %) hybrid hydrogel coating after exposure to xenon light for different times; photographs of the PU cross-linked with P(GA/AAm/OEGMA300)/g-C3N4 (2 wt %) hybrid hydrogel coating stained by pitaya juice and red wine after illumination for different times; photographs of the as-prepared PU and PU cross-linked with P(GA/AAm/OEGMA300)/g-C3N4 hybrid hydrogel coating before staining by cooking oil containing Nile red, after staining, and after rinsing with distilled water thermo-stated at 25 °C for 30 s; scheme for the abrasion measurement; and WCA after the abrasion measurements (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology